Additives

Product Appearance Mix Ratio Data Sheet Comment
MED-4102-1 White 1 PART Download MED-4102-1 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-2 Black 1 PART Download MED-4102-2 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-3 Red 1 PART Download MED-4102-3 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Red
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-4 Orange 1 PART Download MED-4102-4 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Orange
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-5 Yellow 1 PART Download MED-4102-5 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Yellow
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-6 Green 1 PART Download MED-4102-6 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4102-7 Dark Blue 1 PART Download MED-4102-7 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Dark Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-1 White 1 PART Download MED-4502-1 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-2 Black 1 PART Download MED-4502-2 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-3 Red 1 PART Download MED-4502-3 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Red
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-4 Orange 1 PART Download MED-4502-4 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Orange
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-5 Yellow 1 PART Download MED-4502-5 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Yellow
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-6 Green 1 PART Download MED-4502-6 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4502-7 Blue 1 PART Download MED-4502-7 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED-4800-1 White 1 PART Download MED-4800-1 data sheet N/A

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART

View more

MED-4800-2 Black 1 PART Download MED-4800-2 data sheet N/A

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART

View more

MED-4800-3 Red 1 PART Download MED-4800-3 data sheet N/A

Product Details

Property Average Result
Appearance Red
Mix Ratio 1 PART

View more

MED-4800-4 Orange 1 PART Download MED-4800-4 data sheet N/A

Product Details

Property Average Result
Appearance Orange
Mix Ratio 1 PART

View more

MED-4800-5 Yellow 1 PART Download MED-4800-5 data sheet N/A

Product Details

Property Average Result
Appearance Yellow
Mix Ratio 1 PART

View more

MED-4800-6 Green 1 PART Download MED-4800-6 data sheet N/A

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART

View more

MED-4800-7 Dark Blue 1 PART Download MED-4800-7 data sheet N/A

Product Details

Property Average Result
Appearance Dark Blue
Mix Ratio 1 PART

View more

MED-4900-1 White 1 PART Download MED-4900-1 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-2 Black 1 PART Download MED-4900-2 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-3 Red 1 PART Download MED-4900-3 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Red
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-4 Orange 1 PART Download MED-4900-4 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Orange
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-5 Yellow 1 PART Download MED-4900-5 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Yellow
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-6 Green 1 PART Download MED-4900-6 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED-4900-7 Dark Blue 1 PART Download MED-4900-7 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Dark Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED1-4102-2 Black 1 PART Download MED1-4102-2 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED1-4102-7 Blue 1 PART Download MED1-4102-7 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED1-4502-2 Black 1 PART Download MED1-4502-2 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED1-4502-7 Blue 1 PART Download MED1-4502-7 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED1-4800-2 Black 1 PART Download MED1-4800-2 data sheet N/A

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART

View more

MED1-4800-7 Blue 1 PART Download MED1-4800-7 data sheet N/A

Product Details

Property Average Result
Appearance Blue
Mix Ratio 1 PART

View more

MED1-4900-2 Black 1 PART Download MED1-4900-2 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED1-4900-7 Blue 1 PART Download MED1-4900-7 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED2-4102 White 1 PART Download MED2-4102 data sheet 75% BaSO4, Barium Sulfate HCR Masterbatch for Radio Opacity

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment 75% BaSO4, Barium Sulfate HCR Masterbatch for Radio Opacity

View more

MED2-4102-6 Green 1 PART Download MED2-4102-6 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED2-4502 White 1 PART Download MED2-4502 data sheet HCR Masterbatch, 75% BaSO4

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment HCR Masterbatch, 75% BaSO4

View more

MED2-4502-6 Green 1 PART Download MED2-4502-6 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED2-4800 White 1 PART Download MED2-4800 data sheet LSR Masterbatch, 50% BaSO4

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment LSR Masterbatch, 50% BaSO4

View more

MED2-4800-6 Green 1 PART Download MED2-4800-6 data sheet N/A

Product Details

Property Average Result
Appearance Green
Mix Ratio 1 PART

View more

MED2-4900 White 1 PART Download MED2-4900 data sheet 50% BaSO4, Barium Sulfate LSR Masterbatch For Radio Opacity

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment 50% BaSO4, Barium Sulfate LSR Masterbatch For Radio Opacity

View more

MED2-4900-6 Light Green 1 PART Download MED2-4900-6 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Light Green
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED3-4102 White 1 PART Download MED3-4102 data sheet 75% TiO2, Titanium Dioxide Hcrmasterbatch

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment 75% TiO2, Titanium Dioxide Hcrmasterbatch

View more

MED3-4102-8 Violet 1 PART Download MED3-4102-8 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Violet
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED3-4502 White 1 PART Download MED3-4502 data sheet HCR Masterbatch, 75% TiO2

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment HCR Masterbatch, 75% TiO2

View more

MED3-4502-8 Violet 1 PART Download MED3-4502-8 data sheet Masterbatch to add color to HCR platinum cure systems

Product Details

Property Average Result
Appearance Violet
Mix Ratio 1 PART
Comment Masterbatch to add color to HCR platinum cure systems

View more

MED3-4800 White 1 PART Download MED3-4800 data sheet LSR Masterbatch, 50% TiO2

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment LSR Masterbatch, 50% TiO2

View more

MED3-4800-8 Violet 1 PART Download MED3-4800-8 data sheet N/A

Product Details

Property Average Result
Appearance Violet
Mix Ratio 1 PART

View more

MED3-4900 White 1 PART Download MED3-4900 data sheet 50% TiO2, Titanium Dioxide LSR Masterbatch

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment 50% TiO2, Titanium Dioxide LSR Masterbatch

View more

MED3-4900-8 Violet 1 PART Download MED3-4900-8 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Violet
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED4-4900 White 1 PART Download MED4-4900 data sheet Ammonium Bicarbonate LSR Foam Masterbatch

Product Details

Property Average Result
Appearance White
Mix Ratio 1 PART
Comment Ammonium Bicarbonate LSR Foam Masterbatch

View more

MED50-4800-1 Translucent White 1 PART Download MED50-4800-1 data sheet N/A

Product Details

Property Average Result
Appearance Translucent White
Mix Ratio 1 PART

View more

MED50-4800-2 Translucent Black 1 PART Download MED50-4800-2 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Black
Mix Ratio 1 PART

View more

MED50-4800-3 Translucent Red 1 PART Download MED50-4800-3 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Red
Mix Ratio 1 PART

View more

MED50-4800-4 Translucent Orange 1 PART Download MED50-4800-4 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Orange
Mix Ratio 1 PART

View more

MED50-4800-5 Translucent Yellow 1 PART Download MED50-4800-5 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Yellow
Mix Ratio 1 PART

View more

MED50-4800-7 Translucent Dark Blue 1 PART Download MED50-4800-7 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Dark Blue
Mix Ratio 1 PART

View more

MED50-4900-1 Translucent White 1 PART Download MED50-4900-1 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent White
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-2 Translucent Black 1 PART Download MED50-4900-2 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Black
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-3 Translucent Red 1 PART Download MED50-4900-3 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Red
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-4 Translucent Orange 1 PART Download MED50-4900-4 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Orange
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-5 Translucent Yellow 1 PART Download MED50-4900-5 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Yellow
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-6 Translucent Green 1 PART Download MED50-4900-6 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Green
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED50-4900-7 Translucent Dark Blue 1 PART Download MED50-4900-7 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Dark Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED51-4800-2 Black 1 PART Download MED51-4800-2 data sheet N/A

Product Details

Property Average Result
Appearance Black
Mix Ratio 1 PART

View more

MED51-4800-7 Translucent Blue 1 PART Download MED51-4800-7 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Blue
Mix Ratio 1 PART

View more

MED51-4900-7 Translucent Blue 1 PART Download MED51-4900-7 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Blue
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED52-4900-6 Translucent Green 1 PART Download MED52-4900-6 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Green
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

MED53-4900-8 Translucent Violet 1 PART Download MED53-4900-8 data sheet Masterbatch to add color to platinum cure systems

Product Details

Property Average Result
Appearance Translucent Violet
Mix Ratio 1 PART
Comment Masterbatch to add color to platinum cure systems

View more

Adhesives/Sealants

Product Cure System Rheology Work Time Durometer Data Sheet Comment
CF2-3521-2 Platinum Thixotropic / non-slump 1 hours 35 Type A Download CF2-3521-2 data sheet Fuel Resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 117 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 35 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 265 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.28
Tensile 600 psi (4.14 MPa)
Work Time 1 hours
Comment Fuel Resistance

View more

CF5-3521-2 Platinum Thixotropic / non-slump 3.5 hours 30 Type A Download CF5-3521-2 data sheet 50% M fluoro. Black and will RTV in 48 hrs

Product Details

Property Average Result
Cure System Platinum
Viscosity 240,000 cP (240,000 mPa*s)
Durometer 30 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 275 %
Mix Ratio 1:1
Specific Gravity 1.3
Tear 35 ppi (6.17 kN/m)
Tensile 550 psi (3.79 MPa)
Work Time 3.5 hours
Comment 50% M fluoro. Black and will RTV in 48 hrs

View more

CV-1142 Oxime Thixotropic / non-slump N/A 45 Type A Download CV-1142 data sheet For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 35 g/minute
Lap Shear 375 psi (2.59 MPa)
Durometer 45 Type A
Appearance Translucent
Cure 7 days / RTV
Dielectric Strength 1,100 volts/mil (42.9 kV/mm)
Elongation 300 %
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.11
Tack Free Time 20 minutes
Tensile 700 psi (4.83 MPa)
Comment For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

View more

CV-1143 Oxime Thixotropic / non-slump N/A 45 Type A Download CV-1143 data sheet Non-Slump

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 25 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 45 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.1
Tack Free Time 15 minutes
Tensile 800 psi (5.52 MPa)
Comment Non-Slump

View more

CV-2187 Platinum Flowable / Self Leveling 3 hours 35 Type A Download CV-2187 data sheet Tough, self leveling and good adhesion to various metals.

Product Details

Property Average Result
Cure System Platinum
Viscosity 90,000 cP (90,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 400 %
Mix Ratio 10:1
Specific Gravity 1.1
Tack Free Time 15 hours
Tear 75 ppi (13.23 kN/m)
Tensile 925 psi (6.38 MPa)
Work Time 3 hours
Comment Tough, self leveling and good adhesion to various metals.

View more

CV-2287 Platinum Flowable / Self Leveling 3.5 hours 30 Type A Download CV-2287 data sheet Low / High Temperature, Flowable, Fast Cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 85,000 cP (85,000 mPa*s)
Lap Shear 450 psi (3.1 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 900 volts/mil (35.1 kV/mm)
Elongation 400 %
Mix Ratio 10:1
Specific Gravity 1.11
Tear 60 ppi (10.58 kN/m)
Tensile 750 psi (5.17 MPa)
Work Time 3.5 hours
Comment Low / High Temperature, Flowable, Fast Cure

View more

CV-2289 Platinum Flowable / Self Leveling 30 minutes 30 Type A Download CV-2289 data sheet Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 50,000 cP (50,000 mPa*s)
Lap Shear 400 psi (2.76 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Tensile 750 psi (5.17 MPa)
Work Time 30 minutes
Comment Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

View more

CV-2289-1 Platinum Flowable / Self Leveling 30 minutes 34 Type A Download CV-2289-1 data sheet Pourable Elastomer

Product Details

Property Average Result
Cure System Platinum
Rheology Flowable / Self Leveling
Work Time 30 minutes
Durometer 34 Type A
Appearance White
Cure 15 minutes / 150 °C
Cure Type Heat Cure / RTV
Dielectric Strength 955 volts/mil (37.25 kV/mm)
Elongation 343 %
Lap Shear 375 psi (2.6 MPa)
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.12
Tack Free Time 5 hours
Tensile 720 psi (5.0 MPa)
Viscosity 50,000 cP (50,000 mPa*s)

View more

CV-2289-2 Platinum Flowable / Self Leveling 30 minutes 30 Type A Download CV-2289-2 data sheet Pourable Elastomer

Product Details

Property Average Result
Cure System Platinum
Viscosity 52,500 cP (52,500 mPa*s)
Lap Shear 425 psi (2.93 MPa)
Durometer 30 Type A
Appearance Black
Cure 15 minutes / 150 °C
Elongation 400 %
Mix Ratio 1:1
Tack Free Time 5 hours
Tear 50 ppi (8.82 kN/m)
Tensile 750 psi (5.17 MPa)
Work Time 30 minutes
Comment Pourable Elastomer

View more

CV-2500 Platinum Flowable / Self Leveling 2 hours 50 Type A Download CV-2500 data sheet Pourable, Optically Clear

Product Details

Property Average Result
Cure System Platinum
Viscosity 8,000 cP (8,000 mPa*s)
Lap Shear 400 psi (2.76 MPa)
Durometer 50 Type A
Appearance Clear
Cure 15 minutes / 150 °C
Elongation 125 %
Mix Ratio 10:1
Specific Gravity 1.02
Tack Free Time 10 hours
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment Pourable, Optically Clear

View more

CV-2500-2 Platinum Flowable / Self Leveling 3 hours 50 Type A Download CV-2500-2 data sheet Low Viscosity, Fast Cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 8,400 cP (8,400 mPa*s)
Durometer 50 Type A
Appearance Black
Cure 30 minutes / 150 °C
Dielectric Strength 850 volts/mil (33.15 kV/mm)
Elongation 150 %
Mix Ratio 10:1
Specific Gravity 1.05
Tack Free Time 6 hours
Tensile 950 psi (6.55 MPa)
Work Time 3 hours
Comment Low Viscosity, Fast Cure

View more

CV-2510 Alkoxy Flowable / Self Leveling 4 hours 45 Type A Download CV-2510 data sheet Low / High Temperature, Flowable

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 45,000 cP (45,000 mPa*s)
Durometer 45 Type A
Appearance White
Cure 7 days / RTV
Elongation 200 %
Mix Ratio 100:0.5
Specific Gravity 1.19
Tack Free Time 9 hours
Tensile 600 psi (4.14 MPa)
Work Time 4 hours
Comment Low / High Temperature, Flowable

View more

CV-2566 Alkoxy Flowable / Self Leveling 3 hours 55 Type A Download CV-2566 data sheet Pourable RTV Cure, * 1 )Primed Lap Shear 500 psi (3.4 MPa)

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 55,000 cP (55,000 mPa*s)
Lap Shear 500 psi (3.45 MPa)
Durometer 55 Type A
Appearance Rust Red
Cure 7 days / RTV
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 150 %
Mix Ratio 100:0.5
Specific Gravity 1.49
Tack Free Time 8 hours
Tear 40 ppi (7.05 kN/m)
Tensile 950 psi (6.55 MPa)
Thermal Conductivity 0.27 W/(mK)
Work Time 3 hours
Comment Pourable RTV Cure, * 1 )Primed Lap Shear 500 psi (3.4 MPa)

View more

CV-2567 Alkoxy Flowable / Self Leveling 6.5 hours 21 Type A Download CV-2567 data sheet Diluent for Tin Condensation CV Silicones

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 5,000 cP (5,000 mPa*s)
Lap Shear 45 psi (0.31 MPa)
Durometer 21 Type A
Appearance Clear
Cure 7 days / RTV
Elongation 150 %
Mix Ratio 100:0.5
Refractive Index 1.40
Specific Gravity 1.01
Tack Free Time 7.5 hours
Tensile 80 psi (0.55 MPa)
Work Time 6.5 hours
Comment Diluent for Tin Condensation CV Silicones

View more

CV-2568 Alkoxy Flowable / Self Leveling 4 hours 50 Type A Download CV-2568 data sheet Long Worktime, Low Density* 1, )Primed Lap Shear 100 psi (0.69 MPa)

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 125,000 cP (125,000 mPa*s)
Lap Shear 100 psi (0.69 MPa)
Durometer 50 Type A
Appearance Red
Cure 7 days / RTV
Dielectric Strength 645 volts/mil (25.16 kV/mm)
Elongation 60 %
Mix Ratio 100:0.5
Specific Gravity 0.64
Tack Free Time 13 hours
Tensile 175 psi (1.21 MPa)
Work Time 4 hours
Comment Long Worktime, Low Density* 1, )Primed Lap Shear 100 psi (0.69 MPa)

View more

CV-2680-12 Platinum N/A N/A N/A Download CV-2680-12 data sheet Low Outgassing version of R-2682-12.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 250 psi (1.72 MPa)
Appearance Translucent
Application Life 7 minutes
Cure 4 hours / 65 °C
Elongation 400 %
Tear 115 ppi (20.28 kN/m)
Tensile 1,450 psi (10 MPa)
Comment Low Outgassing version of R-2682-12.

View more

CV-2686-12 Platinum N/A N/A N/A Download CV-2686-12 data sheet Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

Product Details

Property Average Result
Cure System Platinum
Appearance Black
Cure 4 hours / 65 °C
Volume Resistivity 150 ohmcm
Comment Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

View more

CV-2688-12 Platinum Thixotropic / Non-slump N/A N/A Download CV-2688-12 data sheet For applications requiring shorter work times, easy clean-up, and consistent bond thickness

Product Details

Property Average Result
Appearance Translucent
Cure 4 hours / 65 °C
Cure System Platinum
Cure Type RTV
Elongation 850 %
Lap Shear 250 psi (1.7 MPa)
Rheology Thixotropic / Non-slump
Substrate Primerless: ABS / Aluminum / Glass / Metal / PEEK / Plastic / PMMA / Polycarbonate / Polyetherimide / Polymide / Polyurethane / Silicone / Stainless steel / Titanium
Tear 115 ppi (20.3 kN/m)
Tensile 1,450 psi (10.0 MPa)

View more

CV1-1142 Oxime Flowable / Self Leveling N/A 30 Type A Download CV1-1142 data sheet Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

Product Details

Property Average Result
Cure System Oxime
Viscosity 13,000 cP (13,000 mPa*s)
Extrusion Rate 70 g/minute
Lap Shear 65 psi (0.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 200 %
Specific Gravity 1.05
Tensile 400 psi (2.76 MPa)
Comment Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

View more

CV1-1142-4 Oxime Flowable / Self Leveling N/A 35 Type A Download CV1-1142-4 data sheet Self-leveling, Built-in UV Tracer

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 60 g/minute
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 200 %
Flow Rate 3 in (76.2 mm)
Mix Ratio 1 PART
Specific Gravity 1.05
Tensile 350 psi (2.41 MPa)
Comment Self-leveling, Built-in UV Tracer

View more

CV1-2289-1 Platinum Flowable / Self Leveling 4 hours 30 Type A Download CV1-2289-1 data sheet White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 52,500 cP (52,500 mPa*s)
Lap Shear 450 psi (3.1 MPa)
Durometer 30 Type A
Appearance White
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 17 hours
Tensile 750 psi (5.17 MPa)
Work Time 4 hours
Comment White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

View more

CV1-2566 Alkoxy Flowable / Self Leveling 3 hours 50 Type A Download CV1-2566 data sheet *1) Primed Lap Shear 650 psi (4.5 MPa)

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 45,000 cP (45,000 mPa*s)
Lap Shear 650 psi (4.48 MPa)
Durometer 50 Type A
Appearance Red
Cure 7 days / RTV
Elongation 160 %
Mix Ratio 100:0.5
Specific Gravity 1.45
Tensile 900 psi (6.21 MPa)
Work Time 3 hours
Comment *1) Primed Lap Shear 650 psi (4.5 MPa)

View more

CV10-2500 Platinum Flowable / Self Leveling 3 hours 50 Type A Download CV10-2500 data sheet High Durometer, Optically Clear

Product Details

Property Average Result
Cure System Platinum
Viscosity 7,500 cP (7,500 mPa*s)
Lap Shear 360 psi (2.48 MPa)
Durometer 50 Type A
Appearance Clear
Cure 15 minutes / 150 °C
Elongation 130 %
Mix Ratio 1:1
Specific Gravity 1.02
Tack Free Time 5 hours
Tensile 1,000 psi (6.9 MPa)
Work Time 3 hours
Comment High Durometer, Optically Clear

View more

CV10-2568 Platinum Flowable / Self Leveling 3 hours 40 Type A Download CV10-2568 data sheet Fast Cure, Low Density*,4 )Primed Lap Shear 175 psi (1.2 MPa)

Product Details

Property Average Result
Cure System Platinum
Viscosity 102,500 cP (102,500 mPa*s)
Lap Shear 175 psi (1.21 MPa)
Durometer 40 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 860 volts/mil (33.54 kV/mm)
Elongation 170 %
Mix Ratio 1:1
Specific Gravity 0.76
Tack Free Time 7 hours
Tensile 235 psi (1.62 MPa)
Work Time 3 hours
Comment Fast Cure, Low Density*,4 )Primed Lap Shear 175 psi (1.2 MPa)

View more

CV14-2500 Platinum Flowable / Self Leveling N/A 30 Type A Download CV14-2500 data sheet Primerless Adhesion

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,600 cP (2,600 mPa*s)
Lap Shear 50 psi (0.34 MPa)
Durometer 30 Type A
Appearance Clear
Cure 1 hours / 65 °C
Elongation 150 %
Mix Ratio 1:1
Specific Gravity 1.01
Tensile 425 psi (2.93 MPa)
Comment Primerless Adhesion

View more

CV15-2500 Platinum Flowable / Self Leveling 3 hours 50 Type A Download CV15-2500 data sheet *4 )Primed Lap Shear 225 psi (1.6 MPa), Optically Clear

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,225 cP (3,225 mPa*s)
Lap Shear 300 psi (2.07 MPa)
Durometer 50 Type A
Appearance Clear
Cure 15 minutes / 150 °C
Elongation 70 %
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Tack Free Time 6 hours
Tensile 850 psi (5.86 MPa)
Work Time 3 hours
Comment *4 )Primed Lap Shear 225 psi (1.6 MPa), Optically Clear

View more

CV16-2500 Platinum Flowable / Self Leveling 2 hours 40 Type A Download CV16-2500 data sheet Low / High Temperature,*4 ) Primed Lap Shear 200 psi (4.1 MPa), Optically Clear

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Lap Shear 200 psi (1.38 MPa)
Durometer 40 Type A
Appearance Clear
Cure 4 hours / 65 °C
Elongation 100 %
Mix Ratio 10:1
Refractive Index 1.43
Specific Gravity 1.04
Tensile 650 psi (4.48 MPa)
Work Time 2 hours
Comment Low / High Temperature,*4 ) Primed Lap Shear 200 psi (4.1 MPa), Optically Clear

View more

CV2-1142 Oxime Thixotropic / non-slump N/A 50 Type A Download CV2-1142 data sheet Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

Product Details

Property Average Result
Cure System Oxime
Durometer 50 Type A
Appearance Translucent
Cure 7 days / RTV
Comment Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

View more

CV2-2289-1 Platinum Flowable / Self Leveling N/A 30 Type A Download CV2-2289-1 data sheet White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 12,300 cP (12,300 mPa*s)
Lap Shear 300 psi (2.07 MPa)
Durometer 30 Type A
Appearance White
Cure 4 hours / 65 °C
Elongation 250 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 20 hours
Tensile 450 psi (3.1 MPa)
Comment White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

View more

CV2-2566 Alkoxy Thixotropic / non-slump 2 hours 55 Type A Download CV2-2566 data sheet *2) Primed Lap Shear 625 psi (4.3 MPa)

Product Details

Property Average Result
Cure System Alkoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 140 %
Mix Ratio 100:0.5
Specific Gravity 1.5
Tear 40 ppi (7.05 kN/m)
Tensile 900 psi (6.21 MPa)
Work Time 2 hours
Comment *2) Primed Lap Shear 625 psi (4.3 MPa)

View more

CV2-2646 Alkoxy Flowable / Self Leveling 2 hours 75 Type A Download CV2-2646 data sheet 0.003 ohmcm at 200 C

Product Details

Property Average Result
Cure System Alkoxy
Lap Shear 185 psi (1.28 MPa)
Durometer 75 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 70 %
Flow Rate 4 in (101.6 mm)
Mix Ratio 100:0.5
Specific Gravity 3.23
Tear 55 ppi (9.7 kN/m)
Tensile 300 psi (2.07 MPa)
Thermal Conductivity 1.5 W/(mK)
Volume Resistivity 0 ohmcm
Work Time 2 hours
Comment 0.003 ohmcm at 200 C

View more

CV3-1142 Oxime Thixotropic / non-slump N/A 45 Type A Download CV3-1142 data sheet Spot Bonding, Available in Black & White

Product Details

Property Average Result
Cure System Oxime
Durometer 45 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 300 %
Mix Ratio 1 PART
Specific Gravity 1.11
Tensile 675 psi (4.66 MPa)
Comment Spot Bonding, Available in Black & White

View more

CV3-2500 Platinum Flowable / Self Leveling 3 hours 40 Type A Download CV3-2500 data sheet Low Viscosity, Potting & Encapsulant, Optically Clear

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,000 cP (3,000 mPa*s)
Durometer 40 Type A
Appearance Clear
Cure 30 minutes / 150 °C
Elongation 100 %
Mix Ratio 10:1
Specific Gravity 1.02
Tack Free Time 6 hours
Tensile 950 psi (6.55 MPa)
Work Time 3 hours
Comment Low Viscosity, Potting & Encapsulant, Optically Clear

View more

CV4-2289-1 Platinum Thixotropic / non-slump 30 minutes 30 Type A Download CV4-2289-1 data sheet Non-flowable

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,150,000 cP (1,150,000 mPa*s)
Lap Shear 325 psi (2.24 MPa)
Durometer 30 Type A
Appearance White
Cure 30 minutes / 150 °C
Elongation 400 %
Mix Ratio 1:1
Tack Free Time 10 hours
Tear 57 ppi (10.05 kN/m)
Tensile 650 psi (4.48 MPa)
Work Time 30 minutes
Comment Non-flowable

View more

CV7-1142-1 Oxime Flowable / Self Leveling N/A 40 Type A Download CV7-1142-1 data sheet Recommended for extended operation at elevated temperatures.

Product Details

Property Average Result
Cure System Oxime
Rheology Flowable / Self Leveling
Durometer 40 Type A
Appearance White
Cure 7 days / RTV
Cure Type RTV
Dielectric Strength 1,180 volts/mil (46.02 kV/mm)
Elongation 300 %
Extrusion Rate 20 g/minute
Flow Rate 0.7 in (17.78 mm)
Mix Ratio 1 PART
Specific Gravity 1.13
Tack Free Time 20 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 700 psi (4.83 MPa)

View more

CV7-2289-1 Platinum Flowable / Self Leveling N/A 30 Type A Download CV7-2289-1 data sheet Primerless Adhesion

Product Details

Property Average Result
Cure System Platinum
Viscosity 228,750 cP (228,750 mPa*s)
Lap Shear 350 psi (2.41 MPa)
Durometer 30 Type A
Appearance White
Cure 15 minutes / 150 °C
Elongation 375 %
Mix Ratio 1:1
Tack Free Time 40 hours
Tensile 700 psi (4.83 MPa)
Comment Primerless Adhesion

View more

EPM-2411-2 Platinum Thixotropic / non-slump N/A 20 Type A Download EPM-2411-2 data sheet Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 300,000 cP (300,000 mPa*s)
Extrusion Rate 0.9 g/minute
Durometer 20 Type A
Appearance Black
Cure 15 minutes / 200 °C
Elongation 700 %
Mix Ratio 1 PART
Specific Gravity 1.15
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 50 ppi (8.82 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

View more

EPM-2412 Platinum Flowable / Self Leveling 20 minutes 30 Type A Download EPM-2412 data sheet Mobile Devices, Displace

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 0.08 g/minute
Durometer 30 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Elongation 450 %
Tensile 850 psi (5.86 MPa)
Thermal Conductivity 0.18 W/(mK)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 20 minutes
Comment Mobile Devices, Displace

View more

EPM-2461 Platinum Thixotropic / non-slump 1 minutes 30 Type A Download EPM-2461 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Viscosity 675,000 cP (675,000 mPa*s)
Lap Shear 325 psi (2.24 MPa)
Durometer 30 Type A
Appearance Black
Cure 24 hours / RTV
Elongation 350 %
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <6 ppm
Mix Ratio 1:1
Operating Temperature -100 °C / 300 °C
Specific Gravity 1.05
Tear 30 ppi (5.29 kN/m)
Tensile 500 psi (3.45 MPa)
Thermal Conductivity 0.22 W/(mK)
Volume Resistivity 535 ohmcm
Work Time 1 minutes
Comment Carbon filled.

View more

EPM-2462 Platinum Thixotropic / non-slump 2.75 hours 85 Type A Download EPM-2462 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 186,200 cP (186,200 mPa*s)
Durometer 85 Type A
Appearance Tan
Cure 30 minutes / 150 C
Elongation 70 %
Ionic Content Cl <5 ppm
Ionic Content K <7 ppm
Ionic Content Na <5 ppm
Mix Ratio 20:1
Specific Gravity 3.39
Tensile 525 psi (3.62 MPa)
Thermal Conductivity 1.2 W/(mK)
Volume Resistivity 0.01 ohmcm
Work Time 2.75 hours

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS-3730-11 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-11 data sheet Lap Shear after 7 days *1) 275 psi (1.9 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 275 psi (1.9 MPa)
Durometer 40 Type A
Appearance Dark Gray
Cure 72 hours / RTV
Elongation 275 %
Mix Ratio 1 PART
Specific Gravity 1.48
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Lap Shear after 7 days *1) 275 psi (1.9 MPa)

View more

FS-3730-2 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-2 data sheet Lap Shear after 7 days *3) 300 psi (2.1 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 200 g/minute
Lap Shear 285 psi (1.97 MPa)
Durometer 40 Type A
Appearance Black
Cure 72 hours / RTV
Elongation 315 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.41
Tack Free Time 10 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 650 psi (4.48 MPa)
Comment Lap Shear after 7 days *3) 300 psi (2.1 MPa)

View more

FS-3775 Acetoxy Flowable / Self Leveling N/A 30 Type A Download FS-3775 data sheet High Temperature, Fuel Resistant

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 250 g/minute
Lap Shear 210 psi (1.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.29
Tack Free Time 8 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 450 psi (3.1 MPa)
Comment High Temperature, Fuel Resistant

View more

FS1-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS1-3730 data sheet Bonds Aggressively

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 150 g/minute
Lap Shear 275 psi (1.9 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / 25 °C
Elongation 425 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.4
Tack Free Time 30 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Bonds Aggressively

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

FS9-3521 Platinum Flowable / Self Leveling 3 hours 29 Type A Download FS9-3521 data sheet 100% F, For applications requiring fuel and solvent resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 50 g/minute
Lap Shear 280 psi (1.93 MPa)
Durometer 29 Type A
Appearance Brown
Cure 24 hours / RTV
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.4
Tensile 750 psi (5.17 MPa)
Work Time 3 hours
Comment 100% F, For applications requiring fuel and solvent resistance

View more

MED-1000 Acetoxy Flowable / Self Leveling N/A 25 Type A Download MED-1000 data sheet Medium flow, high extrusion rate

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 795 %
Extrusion Rate 2.5 g/minute
Specific Gravity 1.08
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 12 minutes
Tear 75 ppi (13.23 kN/m)
Tensile 1,400 psi (9.66 MPa)
Comment Medium flow, high extrusion rate

View more

MED-1011 Acetoxy Flowable / Self Leveling N/A 25 Type A Download MED-1011 data sheet Low flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 725 %
Extrusion Rate 90 g/minute
Flow Rate 1.1 in (27.94 mm)
Specific Gravity 1.12
Stress at Strain 115 psi / 200 % (0.79 MPa / 200 %)
Substrate Primerless: Glass / Polyurethane / Silicone / Aluminum / Titanium / With Primer: Polycarbonate / Stainless steel
Tack Free Time 13 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Comment Low flow

View more

MED-1031 Oxime Thixotropic / non-slump N/A 35 Type A Download MED-1031 data sheet Non-acidic leaving group

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 7 days / RTV
Cure System Oxime
Durometer 35 Type A
Elongation 310 %
Extrusion Rate 70 g/minute
Specific Gravity 1.1
Stress at Strain 415 psi / 200 % (2.86 MPa / 200 %)
Substrate Primerless: Glass / Polyurethane / Aluminum / Silicone / Titanium
Tack Free Time 22 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 840 psi (5.79 MPa)
Comment Non-acidic leaving group

View more

MED-1037 Acetoxy Thixotropic / non-slump N/A 30 Type A Download MED-1037 data sheet Low-slump, solvent-free translucent silicone

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 565 %
Extrusion Rate 2.8 g/minute
Flow Rate 0.2 in (5.08 mm)
Specific Gravity 1.07
Stress at Strain 170 psi / 200 % (1.17 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 9 minutes
Tensile 730 psi (5.03 MPa)
Comment Low-slump, solvent-free translucent silicone

View more

MED-1040 Acetoxy Flowable / Self Leveling N/A 23 Type A Download MED-1040 data sheet High flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 23 Type A
Elongation 340 %
Extrusion Rate 4 g/minute
Flow Rate 2.2 in (55.88 mm)
Specific Gravity 1.03
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium
Tack Free Time 9.5 minutes
Tear 17 ppi (3 kN/m)
Tensile 265 psi (1.83 MPa)
Comment High flow

View more

MED-1131 Oxime Thixotropic / non-slump N/A 35 Type A Download MED-1131 data sheet Non-acidic leaving group

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 7 days / RTV
Cure System Oxime
Durometer 35 Type A
Elongation 330 %
Flow Rate 0.4 in (10.16 mm)
Specific Gravity 1.1
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium
Tack Free Time 20 minutes
Tear 45 ppi (7.94 kN/m)
Tensile 890 psi (6.14 MPa)
Comment Non-acidic leaving group

View more

MED-1137 Acetoxy Thixotropic / non-slump N/A 30 Type A Download MED-1137 data sheet Low-slump, solvent-free translucent silicone

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 560 %
Extrusion Rate 180 g/minute
Flow Rate 0.2 in (5.08 mm)
Specific Gravity 1.07
Stress at Strain 170 psi / 200 % (1.17 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 9 minutes
Tensile 700 psi (4.83 MPa)
Comment Low-slump, solvent-free translucent silicone

View more

MED-1511 Acetoxy Flowable / Self Leveling N/A 25 Type A Download MED-1511 data sheet Low flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 680 %
Extrusion Rate 100 g/minute
Specific Gravity 1.12
Stress at Strain 130 psi / 200 % (0.9 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tack Free Time 12 minutes
Tear 95 ppi (16.75 kN/m)
Tensile 1,440 psi (9.93 MPa)
Comment Low flow

View more

MED-1540 Acetoxy Flowable / Self Leveling N/A 23 Type A Download MED-1540 data sheet High flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 23 Type A
Elongation 340 %
Flow Rate 2.7 in (68.58 mm)
Specific Gravity 1.03
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium
Tack Free Time 9.5 minutes
Tear 17 ppi (3 kN/m)
Tensile 265 psi (1.83 MPa)
Comment High flow

View more

MED-2000 Acetoxy Flowable / Self Leveling N/A 25 Type A Download MED-2000 data sheet Medium flow, high extrusion rate

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 800 %
Extrusion Rate 2.5 g/minute
Specific Gravity 1.08
Stress at Strain 105 psi / 200 % (0.72 MPa / 200 %)
Substrate Primerless: Glass / Polyurethane / Aluminum / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 13 minutes
Tear 80 ppi (14.11 kN/m)
Tensile 1,375 psi (9.48 MPa)
Comment Medium flow, high extrusion rate

View more

MED1-4013 Platinum Thixotropic / non-slump N/A 20 Type A Download MED1-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 24 hours / RTV
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Peel Strength 17 lbf/in (2.98 kN/m)
Specific Gravity 1.11
Stress at Strain 120 psi / 200 % (0.83 MPa / 200 %)
Substrate Primerless: Glass / Aluminum / PMMA / Polycarbonate / Silicone / Polyurethane / With Primer: ABS / Polyetherimide / PEEK / Polycarbonate / Polyimide / Polysulphone / Stainless steel / Polyurethane
Tack Free Time 15 minutes
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED1-4213 Platinum Thixotropic / non-slump 15 minutes 20 Type A Download MED1-4213 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Work Time 15 minutes
Appearance Translucent
Cure 24 hours / 25 °C
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Specific Gravity 1.12
Substrate Primerless: Aluminum / Glass / PMMA / Polyurethane / Silicone / Polycarbonate / With Primer: ABS / Polycarbonate / Polyimide / Polysulphone / Polyurethane / PEEK / Polyetherimide / Stainless steel
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED2-4013 Platinum Thixotropic / non-slump N/A 15 Type A Download MED2-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Durometer 15 Type A
Elongation 800 %
Peel Strength 26 lbf/in (4.55 kN/m)
Specific Gravity 1.12
Stress at Strain 80 psi / 200 % (0.55 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyetherimide / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tack Free Time 15 hours
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED2-4213 Platinum Thixotropic / non-slump 15 hours 15 Type A Download MED2-4213 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Work Time 15 hours
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Durometer 15 Type A
Elongation 800 %
Specific Gravity 1.12
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: Plastic / Polycarbonate / Polyetherimide / Polysulphone / PEEK / Stainless steel / Polyimide / Polyurethane
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED3-4013 Platinum Thixotropic / non-slump N/A 20 Type A Download MED3-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 24 hours / RTV
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Peel Strength 23 lbf/in (4.03 kN/m)
Specific Gravity 1.12
Stress at Strain 125 psi / 200 % (0.86 MPa / 200 %)
Substrate Primerless: Aluminum / PMMA / Polyurethane / Glass / Polycarbonate / Silicone / With Primer: PEEK / Polyetherimide / Polysulphone / ABS / Polycarbonate / Stainless steel / Polyimide / Polyurethane
Tack Free Time 60 minutes
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED3-4213 Platinum Thixotropic / non-slump 60 minutes 20 Type A Download MED3-4213 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Work Time 60 minutes
Appearance Translucent
Cure 24 hours / 25 °C
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Specific Gravity 1.12
Substrate Primerless: Aluminum / Glass / PMMA / Polycarbonate / Polyurethane / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyetherimide / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

R-1130 Oxime Thixotropic / non-slump N/A 35 Type A Download R-1130 data sheet Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 70 g/minute
Lap Shear 485 psi (3.34 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 325 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.1
Tack Free Time 25 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

View more

R-1140 Acetoxy Thixotropic / non-slump N/A 30 Type A Download R-1140 data sheet Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 350 %
Flow Rate 1.5 in (38.1 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.09
Tack Free Time 7 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

View more

R-1400 Platinum Thixotropic / non-slump N/A 19 Type A Download R-1400 data sheet Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400,000 cP (400,000 mPa*s)
Extrusion Rate 120 g/minute
Durometer 19 Type A
Appearance Black
Cure 15 minutes / 200 °C
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Elongation 750 %
Mix Ratio 1 PART
Specific Gravity 1.18
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 110 ppi (19.4 kN/m)
Tensile 825 psi (5.69 MPa)
Comment Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

View more

R-2141 N/A Flowable / Self Leveling 1.5 hours 40 Type A Download R-2141 data sheet N/A

Product Details

Property Average Result
Viscosity 180,000 cP (180,000 mPa*s)
Durometer 40 Type A
Appearance Translucent
Dielectric Strength 630 volts/mil (24.57 kV/mm)
Elongation 250 %
Flow Rate 0.3 in (7.62 mm)
Specific Gravity 1.1
Tack Free Time 4 hours
Tensile 650 psi (4.48 MPa)
Volatile Content 0.3 %
Work Time 1.5 hours

View more

R-2145 Platinum Flowable / Self Leveling 15 minutes 45 Type A Download R-2145 data sheet Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 180 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 15 minutes
Comment Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

View more

R-2160 Platinum Flowable / Self Leveling 1.5 hours 20 Type A Download R-2160 data sheet Iron Red, flowable legacy high performance elastomer at elevated temperatures.

Product Details

Property Average Result
Cure System Platinum
Viscosity 280,000 cP (280,000 mPa*s)
Durometer 20 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Elongation 625 %
Mix Ratio 10:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 315 °C
Specific Gravity 1.2
Tear 140 ppi (24.69 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 1.5 hours
Comment Iron Red, flowable legacy high performance elastomer at elevated temperatures.

View more

R-2186 Platinum Flowable / Self Leveling 2.5 hours 30 Type A Download R-2186 data sheet Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 83,000 cP (83,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 640 volts/mil (24.96 kV/mm)
Elongation 450 %
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 100 ppi (17.64 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 2.5 hours
Comment Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more

R-2550 Alkoxy Flowable / Self Leveling 6 hours 35 Type A Download R-2550 data sheet Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 9,000 cP (9,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 175 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.08
Tear 20 ppi (3.53 kN/m)
Tensile 500 psi (3.45 MPa)
Work Time 6 hours
Comment Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2560 Alkoxy Flowable / Self Leveling 1 minutes 55 Type A Download R-2560 data sheet Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 31,000 cP (31,000 mPa*s)
Lap Shear 385 psi (2.66 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 125 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Specific Gravity 1.41
Tack Free Time 2 hours
Tensile 700 psi (4.83 MPa)
Work Time 1 minutes
Comment Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2630 Platinum Flowable / Self Leveling 15 hours 60 Type A Download R-2630 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Durometer 60 Type A
Appearance Black
Cure 30 minutes / 150 °C
Elongation 95 %
Mix Ratio 10:1
Operating Temperature -65 °C / 200 °C
Specific Gravity 1.1
Tear 40 ppi (7.05 kN/m)
Tensile 690 psi (4.76 MPa)
Volume Resistivity 6 ohmcm
Work Time 15 hours
Comment Carbon filled.

View more

R-2634 Alkoxy Thixotropic / non-slump 3 hours 80 Type A Download R-2634 data sheet 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

Product Details

Property Average Result
Cure System Alkoxy
Extrusion Rate 160 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 80 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 90 %
Flow Rate 1.2 in (30.48 mm)
Mix Ratio 100:0.5
Specific Gravity 3.41
Tear 50 ppi (8.82 kN/m)
Tensile 250 psi (1.72 MPa)
Volume Resistivity 0 ohmcm
Work Time 3 hours
Comment 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

View more

R-2682-12 Platinum N/A N/A N/A Download R-2682-12 data sheet For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 100 psi (0.69 MPa)
Appearance Translucent
Application Life 4 minutes
Cure 4 hours / 65 °C
Comment For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

View more

R1-2145 Platinum Flowable / Self Leveling 1 minutes 45 Type A Download R1-2145 data sheet Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 140 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 190 ppi (33.51 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 1 minutes
Comment Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

View more

R31-2186 Platinum Flowable / Self Leveling 15 minutes 20 Type A Download R31-2186 data sheet RTV Primerless Adhesive;Very fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 142,500 cP (142,500 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 110 psi (0.76 MPa)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 775 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Tear 125 ppi (22.05 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 15 minutes
Comment RTV Primerless Adhesive;Very fast cure.

View more

R32-2186 Platinum Flowable / Self Leveling 15 hours 15 Type A Download R32-2186 data sheet Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 170,000 cP (170,000 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 150 psi (1.03 MPa)
Durometer 15 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 850 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Stress at Strain 35 psi / 100 % (0.24 MPa / 100 %)
Tear 125 ppi (22.05 kN/m)
Tensile 975 psi (6.72 MPa)
Work Time 15 hours
Comment Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

View more

R33-2186 Platinum Flowable / Self Leveling 2 hours 20 Type A Download R33-2186 data sheet RTV Primerless Adhesive;Fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 124,350 cP (124,350 mPa*s)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 725 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 150 ppi (26.46 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment RTV Primerless Adhesive;Fast cure.

View more

R33-2186-1 N/A Flowable / Self Leveling 2 hours 20 Type A Download R33-2186-1 data sheet N/A

Product Details

Property Average Result
Viscosity 80,000 cP (80,000 mPa*s)
Durometer 20 Type A
Appearance White
Elongation 740 %
Specific Gravity 1.12
Tear 135 ppi (23.81 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours

View more

R4-1140 Acetoxy Flowable / Self Leveling N/A 25 Type A Download R4-1140 data sheet Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 100 g/minute
Durometer 25 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 750 %
Flow Rate 2 in (50.8 mm)
Mix Ratio 1 PART
Specific Gravity 1.12
Stress at Strain 110 psi / N/A (0.76 MPa / N/A)
Tack Free Time 10 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Volatile Content 2.4 %
Comment Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

View more

SCV-2585 Platinum Flowable / Self Leveling 1 hours 35 Type A Download SCV-2585 data sheet Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 77,000 cP (77,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.11
Tack Free Time 7 hours
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Work Time 1 hours
Comment Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more

SCV-2586 Platinum Thixotropic / non-slump 4 hours 45 Type A Download SCV-2586 data sheet Fast Cure, Low Density, Primed Lap Shear 175psi

Product Details

Property Average Result
Cure System Platinum
Viscosity 325,000 cP (325,000 mPa*s)
Lap Shear 175 psi (1.21 MPa)
Durometer 45 Type A
Appearance Red
Cure 30 minutes / 150 °C
Elongation 150 %
Mix Ratio 1:1
Specific Gravity 0.74
Tensile 225 psi (1.55 MPa)
Work Time 4 hours
Comment Fast Cure, Low Density, Primed Lap Shear 175psi

View more

SCV-2590 Platinum Flowable / Self Leveling N/A 45 Type A Download SCV-2590 data sheet Pourable

Product Details

Property Average Result
Cure System Platinum
Viscosity 9,500 cP (9,500 mPa*s)
Lap Shear 375 psi (2.59 MPa)
Durometer 45 Type A
Appearance Clear
Cure 15 minutes / 150 °C
Elongation 125 %
Mix Ratio 10:1
Specific Gravity 1.02
Tensile 950 psi (6.55 MPa)
Comment Pourable

View more

SCV-2590-2 Platinum Flowable / Self Leveling 4.5 hours 50 Type A Download SCV-2590-2 data sheet Low Viscosity, Fast Cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 9,500 cP (9,500 mPa*s)
Durometer 50 Type A
Appearance Black
Cure 30 minutes / 150 °C
Dielectric Strength 850 volts/mil (33.15 kV/mm)
Elongation 150 %
Mix Ratio 10:1
Specific Gravity 1.06
Tack Free Time 15 minutes
Tensile 950 psi (6.55 MPa)
Work Time 4.5 hours
Comment Low Viscosity, Fast Cure

View more

SCV1-2590 Platinum Flowable / Self Leveling 4 hours 50 Type A Download SCV1-2590 data sheet *4) Primed Lap Shear 175 psi (1.2 MPa)

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,300 cP (3,300 mPa*s)
Lap Shear 175 psi (1.21 MPa)
Durometer 50 Type A
Appearance Clear
Cure 15 minutes / 150 °C
Elongation 90 %
Mix Ratio 1:1
Specific Gravity 1.02
Tensile 925 psi (6.38 MPa)
Work Time 4 hours
Comment *4) Primed Lap Shear 175 psi (1.2 MPa)

View more

SCV2-2590 Platinum Flowable / Self Leveling N/A 45 Type A Download SCV2-2590 data sheet Low / High Temperature, *4) Primed Lap Shear 250 psi (1.7 MPa)

Product Details

Property Average Result
Cure System Platinum
Viscosity 6,500 cP (6,500 mPa*s)
Lap Shear 250 psi (1.72 MPa)
Durometer 45 Type A
Appearance Clear
Cure 4 hours / 65 °C
Elongation 85 %
Mix Ratio 10:1
Refractive Index 1.43
Specific Gravity 1.04
Tensile 475 psi (3.28 MPa)
Comment Low / High Temperature, *4) Primed Lap Shear 250 psi (1.7 MPa)

View more

Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV-1144-0 Oxime 240 cP 60 % N/A Download CV-1144-0 data sheet 60% Solids, Atomic Oxygen Protective Overcoat

Product Details

Property Average Result
Viscosity 240 cP (240 mPa*s)
Non Volatile Content 60 %
Appearance Clear
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1
Comment 60% Solids, Atomic Oxygen Protective Overcoat

View more

CV-1146-2 Oxime 2,400 cP 72 % N/A Download CV-1146-2 data sheet 72% Solids

Product Details

Property Average Result
Viscosity 2,400 cP (2,400 mPa*s)
Non Volatile Content 72 %
Appearance Black
Cure 7 days / RTV
Cure System Oxime
Dielectric Strength 845 volts/mil (32.96 kV/mm)
Mix Ratio 1 PART
Specific Gravity 1.26
Comment 72% Solids

View more

CV-1152 Oxime 7,300 cP N/A N/A Download CV-1152 data sheet Soft, very low modulus coating

Product Details

Property Average Result
Viscosity 7,300 cP (7,300 mPa*s)
Appearance Translucent
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.01
Comment Soft, very low modulus coating

View more

CV1-1144-0 Oxime 850 cP 50 % N/A Download CV1-1144-0 data sheet 50% Solids

Product Details

Property Average Result
Viscosity 850 cP (850 mPa*s)
Non Volatile Content 50 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.11
Comment 50% Solids

View more

CV1-1146-2 Oxime 1,125 cP N/A N/A Download CV1-1146-2 data sheet N/A

Product Details

Property Average Result
Viscosity 1,125 cP (1,125 mPa*s)
Appearance Black
Tack Free Time 2 hours
Cure System Oxime

View more

CV1-1148 Oxime 5,000 cP 40 % N/A Download CV1-1148 data sheet 40% Solids

Product Details

Property Average Result
Viscosity 5,000 cP (5,000 mPa*s)
Non Volatile Content 40 %
Appearance Black
Tack Free Time 40 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.07
Comment 40% Solids

View more

CV2-1147 Oxime 2,000 cP 60 % N/A Download CV2-1147 data sheet 60% Solids, Non-blocking Overcoat

Product Details

Property Average Result
Viscosity 2,000 cP (2,000 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 2 hours
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.12
Comment 60% Solids, Non-blocking Overcoat

View more

CV3-1144-1 Oxime 900 cP 60 % N/A Download CV3-1144-1 data sheet 60% Solids

Product Details

Property Average Result
Viscosity 900 cP (900 mPa*s)
Non Volatile Content 60 %
Appearance White
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Comment 60% Solids

View more

MED-2014 Platinum 1,800 cP 35 % N/A Download MED-2014 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,800 cP (1,800 mPa*s)
Non Volatile Content 35 %
Appearance Translucent
Cure 60 minutes / 50 °C 60 minutes / 150 °C 3 minutes / RTV
Elongation 900 %
Mix Ratio 1 PART
Solvent Xylene
Tear 160 ppi (28.22 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-2214 Platinum 3,700 cP 35 % 35 Type A Download MED-2214 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,700 cP (3,700 mPa*s)
Non Volatile Content 35 %
Durometer 35 Type A
Appearance Translucent
Cure 60 minutes / 50 °C
Elongation 850 %
Mix Ratio 1 Part
Tear 170 ppi (29.98 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-4159 Amine 200 cSt 53 % N/A Download MED-4159 data sheet Low Crosslink Density, Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 200 cSt
Non Volatile Content 53 %
Appearance Clear
Cure 7 days / RTV
Mix Ratio 1 PART
Solvent Stoddard Solvent & IPA
Comment Low Crosslink Density, Amino Functional Lubricious Silicone Coating

View more

MED-4162 Non-Curing 27,000 cP 31 % N/A Download MED-4162 data sheet Lubricious Coating

Product Details

Property Average Result
Cure System Non-Curing
Viscosity 27,000 cP (27,000 mPa*s)
Non Volatile Content 31 %
Appearance Translucent
Mix Ratio 1 PART
Solvent Xylene
Comment Lubricious Coating

View more

MED-6400 Platinum 860 cP 35 % 30 Type A Download MED-6400 data sheet 1.43 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 860 cP (860 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Cure Type Heat Cure
Elongation 850 %
Mix Ratio 1:1
Refractive Index 1.43
Rheology Flowable/Self Leveling
Tear 160 ppi (28.22 kN/m)
Tensile 1,600 psi (11.03 MPa)

View more

MED-6600 Platinum 350 cP 35 % 25 Type A Download MED-6600 data sheet 1.46 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 350 cP (350 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Refractive Index 1.46
Specific Gravity 1.1
Stress at Strain 300 psi / 300 % (2.07 Mpa / 300 %)
Tear 160 ppi (28.22 kN/m)
Tensile 1,200 psi (8.28 MPa)
Work Time 24 hours
Comment 1.46 R.I. in Xylene

View more

MED-6601 N/A N/A N/A 24 Type A Download MED-6601 data sheet 100% solids

Product Details

Property Average Result
Durometer 24 Type A
Appearance Translucent
Elongation 800 %
Stress at Strain 320 psi / 300 % (2.21 Mpa / 300 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 100% solids

View more

MED-6605 Acetoxy 700 cP 29 % 25 Type A Download MED-6605 data sheet One Part, in Xylene

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 980 %
Mix Ratio 1 PART
Refractive Index 1.40
Specific Gravity 1.09
Stress at Strain 110 psi / 300 % (0.76 Mpa / 300 %)
Tear 120 ppi (21.16 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part, in Xylene

View more

MED-6615 Platinum 65 cP 32 % 72 Type 00 Download MED-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyimide / Polysulphone / Polyetherimide / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED-6640 Platinum 3,000 cP 20 % 40 Type A Download MED-6640 data sheet Ultra High Tear, in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,000 cP (3,000 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 24 hours
Comment Ultra High Tear, in Xylene

View more

MED-6655 Acetoxy 700 cP 60 % 35 Type A Download MED-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Cure Type RTV
Elongation 425 %
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Tack Free Time 80 minutes
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED-6670 Platinum N/A 25 % N/A Download MED-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Specific Gravity 0.96
Work Time 24 hours
Comment Low Coefficient of Friction Coating

View more

MED-6671 Acetoxy N/A N/A N/A Download MED-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED1-4161 Condensation 140 cSt 33 % 25 Type 00 Download MED1-4161 data sheet 25 '00' durometer lubricious coating

Product Details

Property Average Result
Cure System Condensation
Viscosity 140 cSt (121.43 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 Part
Solvent Xylene
Specific Gravity 0.87
Comment 25 '00' durometer lubricious coating

View more

MED10-4161 Amine 140 cSt 33 % 25 Type 00 Download MED10-4161 data sheet Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 140 cSt (120.04 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 PART
Solvent Xylene
Specific Gravity 0.86
Comment Amino Functional Lubricious Silicone Coating

View more

MED10-6400 Platinum 800 cP 35 % 30 Type A Download MED10-6400 data sheet 1.43 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 800 cP (800 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Solvent Xylene
Tear 150 ppi (26.46 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment 1.43 R.I.

View more

MED10-6600 Platinum 400 cP 35 % 25 Type A Download MED10-6600 data sheet 1.46 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400 cP (400 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 750 %
Mix Ratio 1:1
Refractive Index 1.46
Solvent Xylene
Stress at Strain 325 psi / 300 % (2.24 Mpa / 300 %)
Tear 145 ppi (25.57 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 1.46 R.I.

View more

MED10-6605 Acetoxy 700 cP 29 % 25 Type A Download MED10-6605 data sheet One Part

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 950 %
Mix Ratio 1 PART
Solvent Xylene
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part

View more

MED10-6607 Oxime 6,000 cP 35 % 40 Type A Download MED10-6607 data sheet One Part

Product Details

Property Average Result
Cure System Oxime
Viscosity 6,000 cP (6,000 mPa*s)
Non Volatile Content 35 %
Durometer 40 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 650 %
Mix Ratio 1 PART
Solvent Naptha
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment One Part

View more

MED10-6615 Platinum 65 cP 32 % 72 Type 00 Download MED10-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: PEEK / Polycarbonate / Polyetherimide / ABS / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED10-6640 Platinum 2,500 cP 20 % 40 Type A Download MED10-6640 data sheet Ultra High Tear

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,500 cP (2,500 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Solvent Xylene
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment Ultra High Tear

View more

MED10-6655 Acetoxy 700 cP 60 % 35 Type A Download MED10-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Elongation 425 %
Mix Ratio 1 PART
Solvent Butyl Acetate
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED10-6670 Platinum N/A 25 % N/A Download MED10-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Solvent Xylene

View more

MED10-6671 Acetoxy N/A N/A N/A Download MED10-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED11-6604 Acetoxy 250 cP 50 % 15 Type A Download MED11-6604 data sheet One Part, Smooth Finish

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 250 cP (250 mPa*s)
Non Volatile Content 50 %
Durometer 15 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 375 %
Mix Ratio 1 PART
Solvent THF
Specific Gravity 0.99
Tear 15 ppi (2.65 kN/m)
Tensile 75 psi (0.52 MPa)
Comment One Part, Smooth Finish

View more

MED16-6606 Acetoxy 95 cP 30 % 20 Type A Download MED16-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Solvent Heptane
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,200 psi (8.28 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more

MED6-6606 Acetoxy 95 cP 30 % 20 Type A Download MED6-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 3 days / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Specific Gravity 1.11
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 115 ppi (20.28 kN/m)
Tensile 1,190 psi (8.21 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more

R-1008-0 Oxime 1,300 cP 70 % 23 Type A Download R-1008-0 data sheet N/A

Product Details

Property Average Result
Viscosity 1,300 cP (1,300 mPa*s)
Non Volatile Content 70 %
Appearance Translucent
Dielectric Strength 513 volts/mil (20.01 kV/mm)
Durometer 23 Type A
Elongation 223 %
Tack Free Time 50 minutes
Tensile 235 psi (1.62 MPa)
Thermal Conductivity 0.17 W/(mK)

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1077 N/A 3,400 cP 60 % 40 Type A Download R-1077 data sheet N/A

Product Details

Property Average Result
Viscosity 3,400 cP (3,400 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 20 minutes
Cure 6 days / RTV
Durometer 40 Type A
Elongation 330 %
Tensile 745 psi (5.14 MPa)

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1099 Condensation 6,600 cP 30 % 40 Type A Download R-1099 data sheet N/A

Product Details

Property Average Result
Viscosity 6,600 cP (6,600 mPa*s)
Non Volatile Content 30 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Condensation
Dielectric Strength 635 volts/mil (24.77 kV/mm)
Durometer 40 Type A
Elongation 570 %
Mix Ratio 1 Part
Tensile 1,050 psi (7.24 MPa)

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2180-2 Platinum 3,275 cP 20 % 45 Type A Download R-2180-2 data sheet Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

Product Details

Property Average Result
Viscosity 3,275 cP (3,275 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 30 minutes / RTV 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 45 Type A
Elongation 1,000 %
Mix Ratio 1:1
Stress at Strain 140 psi / 100 % (0.97 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,650 psi (11.38 MPa)
Comment Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

View more

R-2182 Platinum 24 cP 25 % N/A Download R-2182 data sheet Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 24 cP (24 mPa*s)
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Cure System Platinum
Mix Ratio 1:1
Post Cure 5 minutes / 150 °C
Specific Gravity 0.96
Work Time 24 hours
Comment Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

R-3975 Acetoxy 1,625 cP 60 % 25 Type A Download R-3975 data sheet Dispersion Coating, 60% Solids

Product Details

Property Average Result
Viscosity 1,625 cP (1,625 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.29
Tear 35 ppi (6.17 kN/m)
Tensile 425 psi (2.93 MPa)
Comment Dispersion Coating, 60% Solids

View more

R3-1075 Oxime 3,300 cP 60 % 40 Type A Download R3-1075 data sheet Dispersion Coating / Conformal, 60% Solids

Product Details

Property Average Result
Viscosity 3,300 cP (3,300 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 80 minutes
Cure 7 days / 25 °C
Cure System Oxime
Dielectric Strength 1,250 volts/mil (48.75 kV/mm)
Durometer 40 Type A
Elongation 350 %
Mix Ratio 1 PART
Operating Temperature -65 °C / 240 °C
Solvent Xylene
Specific Gravity 1.06
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Dispersion Coating / Conformal, 60% Solids

View more

Elastomer Gels

Product INCI Name D4 Content Viscosity Appearance Data Sheet Comment
CXG-1101 Cyclopentasiloxane (and) Dimethicone/Vinyl Dimethicone Crosspolymer <0.05 % 550,000 cP Clear Download CXG-1101 data sheet 12% Solids Elastomer Gel Dispersed in D5

Product Details

Property Average Result
INCI Name Cyclopentasiloxane (and) Dimethicone/Vinyl Dimethicone Crosspolymer
D4 Content <0.05 %
Viscosity 550,000 cP (550,000 mPa*s)
Appearance Clear
Non Volatile Content 12 %
Refractive Index 1.40
Specific Gravity 0.96
Comment 12% Solids Elastomer Gel Dispersed in D5

View more

CXG-1103 Cyclopentasiloxane (and) Cyclohexasiloxane (and) Dimethicone/Vinyl Dimethicone Crosspolymer <0.05 % 60,000 cP Clear Download CXG-1103 data sheet 8% Solids Elastomer Gel Dispersed in D5 and D6

Product Details

Property Average Result
INCI Name Cyclopentasiloxane (and) Cyclohexasiloxane (and) Dimethicone/Vinyl Dimethicone Crosspolymer
D4 Content <0.05 %
Viscosity 60,000 cP (60,000 mPa*s)
Appearance Clear
Non Volatile Content 8 %
Refractive Index 1.40
Specific Gravity 0.96
Comment 8% Solids Elastomer Gel Dispersed in D5 and D6

View more

CXG-1104 Dimethicone (and) Dimethicone/Vinyl Dimethicone Crosspolymer <0.05 % 635,000 cP Clear Download CXG-1104 data sheet 12% Solids Elastomer Gel Dispersed in Low Viscosity Dimethicone Fluid

Product Details

Property Average Result
INCI Name Dimethicone (and) Dimethicone/Vinyl Dimethicone Crosspolymer
D4 Content <0.05 %
Viscosity 635,000 cP (635,000 mPa*s)
Appearance Clear
Refractive Index 1.40
Specific Gravity 0.92
Comment 12% Solids Elastomer Gel Dispersed in Low Viscosity Dimethicone Fluid

View more

Electrically Conductive/Static Dissipative

Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
CV-1500 3 ohmcm N/A Oxime 80 Type A 650 psi Download CV-1500 data sheet Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

Product Details

Property Average Result
Volume Resistivity 3 ohmcm
Cure System Oxime
Durometer 80 Type A
Tensile 650 psi (4.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 20 %
Flow Rate 0 in
Lap Shear 325 psi (2.24 MPa)
Specific Gravity 1.25
Tack Free Time 10 minutes
Comment Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

View more

CV-2640 2.5 ohmcm N/A Platinum 75 Type A 475 psi Download CV-2640 data sheet 2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled

Product Details

Property Average Result
Volume Resistivity 2.5 ohmcm
Cure System Platinum
Durometer 75 Type A
Tensile 475 psi (3.28 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 90 %
Lap Shear 250 psi (1.72 MPa)
Mix Ratio 10:1
Specific Gravity 1.19
Work Time 2 hours
Comment 2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled

View more

CV-2644 0.01 ohmcm 224,500 cP Platinum 85 Type A 525 psi Download CV-2644 data sheet 0.005 ohmcm, *22) 1.2 W/mK

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Viscosity 224,500 cP (224,500 mPa*s)
Cure System Platinum
Durometer 85 Type A
Tensile 525 psi (3.62 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Elongation 86 %
Mix Ratio 20:1
Specific Gravity 3.39
Thermal Conductivity 1.2 W/(mK)
Work Time 2.75 hours
Comment 0.005 ohmcm, *22) 1.2 W/mK

View more

CV-2646 0.01 ohmcm N/A Alkoxy 80 Type A 400 psi Download CV-2646 data sheet Electrically Conductive, 0.007 ohmcm

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Alkoxy
Durometer 80 Type A
Tensile 400 psi (2.76 MPa)
Appearance Tan
Cure 10 days / RTV
Elongation 90 %
Lap Shear 325 psi (2.24 MPa)
Mix Ratio 100:0.5
Specific Gravity 3.86
Tear 60 ppi (10.58 kN/m)
Thermal Conductivity 1 W/(mK)
Work Time 3.5 hours
Comment Electrically Conductive, 0.007 ohmcm

View more

CV1-2640 25 ohmcm N/A Platinum 40 Type A 525 psi Download CV1-2640 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 25 ohmcm
Cure System Platinum
Durometer 40 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 2 hours / 65 °C
Elongation 225 %
Extrusion Rate 300 g/minute
Mix Ratio 10:1
Specific Gravity 1.07
Comment Carbon filled.

View more

CV1-2646 0.01 ohmcm N/A Alkoxy 80 Type A 400 psi Download CV1-2646 data sheet 0.005 ohmcm

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Alkoxy
Durometer 80 Type A
Tensile 400 psi (2.76 MPa)
Appearance Tan
Cure 10 days / RTV
Elongation 90 %
Lap Shear 325 psi (2.24 MPa)
Mix Ratio 100:0.5
Specific Gravity 3.86
Tear 60 ppi (10.58 kN/m)
Thermal Conductivity 1 W/(mK)
Work Time 3.5 hours
Comment 0.005 ohmcm

View more

CV2-1148 9,000,000,000 ohmcm N/A Oxime 45 Type A N/A Download CV2-1148 data sheet 100% Solids

Product Details

Property Average Result
Volume Resistivity 9,000,000,000 ohmcm
Cure System Oxime
Durometer 45 Type A
Appearance Black
Cure 7 days / RTV
Mix Ratio 1 PART
Specific Gravity 1.07
Comment 100% Solids

View more

CV2-2640 1 ohmcm 675,000 cP Platinum 30 Type A 500 psi Download CV2-2640 data sheet Carbon Black Filled

Product Details

Property Average Result
Volume Resistivity 1 ohmcm
Viscosity 675,000 cP (675,000 mPa*s)
Cure System Platinum
Durometer 30 Type A
Tensile 500 psi (3.45 MPa)
Appearance Black
Cure 24 hours / RTV
Elongation 350 %
Mix Ratio 1:1
Specific Gravity 1.06
Tear 30 ppi (5.29 kN/m)
Thermal Conductivity 0.22 W/(mK)
Work Time 1 hours
Comment Carbon Black Filled

View more

CV2-2644 0 ohmcm N/A Platinum 85 Type A 500 psi Download CV2-2644 data sheet 0.004 ohmcm

Product Details

Property Average Result
Volume Resistivity 0 ohmcm
Cure System Platinum
Durometer 85 Type A
Tensile 500 psi (3.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Elongation 100 %
Mix Ratio 20:1
Specific Gravity 3.04
Work Time 2.5 hours
Comment 0.004 ohmcm

View more

CV3-2640 2,200,000 ohmcm 14,100 cP Platinum 25 Type A 70 psi Download CV3-2640 data sheet Carbon filled. Designed for broad operating temperature.

Product Details

Property Average Result
Volume Resistivity 2,200,000 ohmcm
Viscosity 14,100 cP (14,100 mPa*s)
Cure System Platinum
Durometer 25 Type A
Tensile 70 psi (0.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 120 %
Lap Shear 50 psi (0.34 MPa)
Mix Ratio 1:1
Specific Gravity 1.01
Tack Free Time 10 hours
Comment Carbon filled. Designed for broad operating temperature.

View more

R-1505 8 ohmcm N/A Oxime 75 Type A 525 psi Download R-1505 data sheet 8 ohmcm. Static Dissipation

Product Details

Property Average Result
Volume Resistivity 8 ohmcm
Cure System Oxime
Durometer 75 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 7 days / 25 °C
Dielectric Strength 10 volts/mil (0.39 kV/mm)
Elongation 25 %
Flow Rate 0.1 in (2.54 mm)
Lap Shear 290 psi (2 MPa)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.23
Tack Free Time 10 minutes
Thermal Conductivity 0.3 W/(mK)
Comment 8 ohmcm. Static Dissipation

View more

R-2631 70 ohmcm N/A Platinum 45 Type A 615 psi Download R-2631 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 70 ohmcm
Cure System Platinum
Durometer 45 Type A
Tensile 615 psi (4.24 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 275 %
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Tear 55 ppi (9.7 kN/m)
Comment Carbon filled.

View more

R-2637 0.01 ohmcm N/A Platinum 60 Type A 210 psi Download R-2637 data sheet Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 60 Type A
Tensile 210 psi (1.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Dielectric Strength 5 volts/mil (0.2 kV/mm)
Elongation 275 %
Mix Ratio 20:1
Specific Gravity 3.6
Tack Free Time 5 hours
Thermal Conductivity 1.5 W/(mK)
Work Time 4 hours
Comment Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

View more

SCV-2596 2.5 ohmcm N/A Platinum 75 Type A 475 psi Download SCV-2596 data sheet Electrically Conductive, 2.5 ohmcm, Carbon Fiber Filled

Product Details

Property Average Result
Volume Resistivity 2.5 ohmcm
Cure System Platinum
Durometer 75 Type A
Tensile 475 psi (3.28 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 90 %
Lap Shear 250 psi (1.72 MPa)
Lap Shear 250 psi (1.72 MPa)
Mix Ratio 10:1
Specific Gravity 1.19
Work Time 2 hours

View more

SCV1-2596 0.01 ohmcm N/A Platinum 85 Type A 450 psi Download SCV1-2596 data sheet Electricaly Conductive, 0.005 ohmcm ,*21, 22) 1.2 W /mK

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 85 Type A
Tensile 450 psi (3.1 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Mix Ratio 20:1
Specific Gravity 3.42
Thermal Conductivity 1.2 W/(mK)
Work Time 2.5 hours
Comment Electricaly Conductive, 0.005 ohmcm ,*21, 22) 1.2 W /mK

View more

Encapsulation Technology

Product INCI Name D4 Content Viscosity Appearance Data Sheet Comment
CES-1104 Dimethicone and Aqua and Glycerin and Pentylene Glycol and Dimethicone/Vinyl Dimethicone Crosspolymer and Phenoxyethanol and Carbomer and Amodimethicone and Sodium Hydroxide and Disodium EDTA <0.05 % 60,000 cP Translucent Download CES-1104 data sheet Encapsulated Silicone with 12% CXG-1104

Product Details

Property Average Result
D4 Content <0.05 %
Viscosity 60,000 cP (60,000 mPa*s)
Appearance Translucent
Refractive Index 1.40
Specific Gravity 1.03
Comment Encapsulated Silicone with 12% CXG-1104

View more

Fluids

Product Substrate Volatile Content Viscosity Data Sheet Comment
FS-3602 Silicone 0.1 % N/A Download FS-3602 data sheet N/A

Product Details

Property Average Result
Volatile Content 0.1 %
Appearance Translucent
Refractive Index 1.39

View more

MED-360 Glass / Metal / Plastic 0.1 % 100 cP / 350 cP / 1,000 cP / 12,500 cP Download MED-360 data sheet Dimethyl Polymer

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 100 cP / 350 cP / 1,000 cP / 12,500 cP (100 mPa*s / 350 mPa*s / 1,000 mPa*s / 12,500 mPa*s)
Appearance Translucent
Mix Ratio 1 PART
Refractive Index 1.40
Specific Gravity 0.97
Substrate Glass / Metal / Plastic
Comment Dimethyl Polymer

View more

MED-361 Glass / Metal / Plastic 0.1 % 100 cP / 350 cP / 1,000 cP / 12,500 cP Download MED-361 data sheet Dimethyl Polymer

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 100 cP / 350 cP / 1,000 cP / 12,500 cP (100 mPa*s / 350 mPa*s / 1,000 mPa*s / 12,500 mPa*s)
Appearance Clear
Substrate Glass / Metal / Plastic
Comment Dimethyl Polymer

View more

MED-366 N/A 0.1 % 1,000 cP Download MED-366 data sheet Highly purified Dimethyl Polymer

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 1,000 cP (1,000 mPa*s)
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 Part
Refractive Index 1.40
Specific Gravity 0.97
Comment Highly purified Dimethyl Polymer

View more

MED-367 N/A 0.1 % 5,000 cP Download MED-367 data sheet Highly purified Dimethyl Polymer

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 5,000 cP (5,000 mPa*s)
Appearance Translucent
Cure System Non-Curing
Mix Ratio 1 Part
Refractive Index 1.40
Specific Gravity 0.97
Comment Highly purified Dimethyl Polymer

View more

MED-400 Silicone 0.3 % 350 cP / 1,000 cP / 12,500 cP Download MED-400 data sheet Fluorosilicone Polymer

Product Details

Property Average Result
Volatile Content 0.3 %
Viscosity 350 cP / 1,000 cP / 12,500 cP (350 mPa*s / 1,000 mPa*s / 12,500 mPa*s)
Substrate Silicone
Comment Fluorosilicone Polymer

View more

MED-420 Silicone 0.1 % 350 cP / 1,000 cP / 12,500 cP Download MED-420 data sheet Methyl Fluoro Copolymer (Low Fluoro Content)

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 350 cP / 1,000 cP / 12,500 cP (350 mPa*s / 1,000 mPa*s / 12,500 mPa*s)
Substrate Silicone
Comment Methyl Fluoro Copolymer (Low Fluoro Content)

View more

MED-460 Silicone 0.1 % 350 cP / 1,000 cP / 12,500 cP Download MED-460 data sheet Methyl Fluoro Copolymer (High Fluoro Content)

Product Details

Property Average Result
Volatile Content 0.1 %
Viscosity 350 cP / 1,000 cP / 12,500 cP (350 mPa*s / 1,000 mPa*s / 12,500 mPa*s)
Substrate Silicone
Comment Methyl Fluoro Copolymer (High Fluoro Content)

View more

PLY-7602 N/A N/A N/A Download PLY-7602 data sheet A processing aid or plasticizer for elastomeric systems

Product Details

Property Average Result
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 PART
Non Volatile Content 52%
Rheology Flowable / Self Leveling
Special Feature Phenyl processing aid
Comment A processing aid or plasticizer for elastomeric systems

View more

PLY-7700 N/A 48 % 6 cSt Download PLY-7700 data sheet Low viscosity fluid

Product Details

Property Average Result
Volatile Content 48 %
Viscosity 6 cSt
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Special Feature Ethoxy functional
Specific Gravity 0.95
Comment Low viscosity fluid

View more

S-7200 Glass / Metal / Plastic 2 % 7,000,000 cP Download S-7200 data sheet 100% Dimethylsiloxane non-reactive polymer. Custom viscosities available.

Product Details

Property Average Result
Viscosity 7,000,000 cP (7,000,000 mPa*s)
Volatile Content 2 %
Specific Gravity 1
Appearance Clear
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Operating Temperature -40 °C / 200 °C
Refractive Index 1.40
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment 100% Dimethylsiloxane non-reactive polymer. Custom viscosities available.

View more

S-7400 Glass / Metal / Plastic 4 % 60,000 cP Download S-7400 data sheet Recommend for extreme temperature (-100°C to 250°C). Higher and custom viscosities available.

Product Details

Property Average Result
Substrate Glass / Metal / Plastic
Volatile Content 4 %
Viscosity 60,000 cP
Appearance Translucent
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Operating Temperature -65 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.1
Volume Resistivity 1,000,000,000,000,000 ohmcm

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

CF3-2350 25 lbs/ft³ 90,000 cP Platinum N/A Gray Download CF3-2350 data sheet Useful where stability at higher and lower temperatures is required.

Product Details

Property Average Result
Foam Density 25 lbs/ft³ (0.4 g/cm³)
Viscosity 90,000 cP (90,000 mPa*s)
Cure System Platinum
Appearance Gray
Cure 45 minutes / 100 °C
Cure Type RTV
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.1

View more

CV-2391 20 lbs/ft3 3,000 cP Platinum 6 minutes White Download CV-2391 data sheet Cure in place versatile low outgassing foam, application life 6 minutes

Product Details

Property Average Result
Viscosity 3,000 cP (3,000 mPa*s)
Cure System Platinum
Foam Density 20 lbs/ft3 (0.32 g/cm3)
Application Life 6 minutes
Appearance White
Cure 60 minutes / RTV
Mix Ratio 1:10
Comment Cure in place versatile low outgassing foam, application life 6 minutes

View more

MED-2310 N/A 40,000 cP Platinum 2 minutes White Download MED-2310 data sheet Low Density

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Application Life 2 minutes
Appearance White
Mix Ratio 1:1
Comment Low Density

View more

MED10-2310 N/A 40,000 cP Platinum 2 minutes White Download MED10-2310 data sheet Low Density

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Application Life 2 minutes
Appearance White
Mix Ratio 1:1
Comment Low Density

View more

R-2360 12 lbs/ft3 40,000 cP Platinum 2 minutes White Download R-2360 data sheet Flexible cure in place low density foam. Application life 2 minutes.

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Foam Density 12 lbs/ft3 (0.19 g/cm3)
Application Life 2 minutes
Appearance White
Cure 20 minutes / RTV
Mix Ratio 1:1
Comment Flexible cure in place low density foam. Application life 2 minutes.

View more

R-2370 10 lbs/ft3 4,700 cP Tin 28 minutes Tan Download R-2370 data sheet Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

Product Details

Property Average Result
Viscosity 4,700 cP (4,700 mPa*s)
Cure System Tin
Foam Density 10 lbs/ft3 (0.16 g/cm3)
Application Life 28 minutes
Appearance Tan
Cure 10 minutes / RTV
Mix Ratio 100:6
Non Volatile Content 100 %
Comment Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

View more

SFM5-2350 25 lbs/ft3 52,500 cP Platinum N/A Black Download SFM5-2350 data sheet Cure in place versatile tough foam. Application life 6 minutes.

Product Details

Property Average Result
Viscosity 52,500 cP (52,500 mPa*s)
Cure System Platinum
Foam Density 25 lbs/ft3 (0.4 g/cm3)
Appearance Black
Cure 33 minutes / 100 °C
Dielectric Strength 190 volts/mil (7.41 kV/mm)
Mix Ratio 1:1
Specific Gravity 1.1
Volume Resistivity 2,200,000,000,000,000 ohmcm
Work Time 23 minutes
Comment Cure in place versatile tough foam. Application life 6 minutes.

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
CV-8151 2,500 cP 4 mm 30 hours 1:1 Download CV-8151 data sheet Low Viscosity, Penetration 4.0 mm

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 4 mm
Work Time 30 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Comment Low Viscosity, Penetration 4.0 mm

View more

CV-8251 1,800 cP 3 mm 24 hours 1:1 Download CV-8251 data sheet Low/High Temperature, Penetration 3 mm

Product Details

Property Average Result
Viscosity 1,800 cP (1,800 mPa*s)
Penetration 3 mm
Work Time 24 hours
Appearance Clear
Cure 40 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Comment Low/High Temperature, Penetration 3 mm

View more

EPM-2480 2,500 cP 4 mm 30 hours 1:1 Download EPM-2480 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 4 mm
Work Time 30 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <2 ppm
Mix Ratio 1:1
Volume Resistivity 100,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

EPM-2482 1,800 cP 3 mm N/A 1:1 Download EPM-2482 data sheet Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

Product Details

Property Average Result
Viscosity 1,800 cP (1,800 mPa*s)
Penetration 3 mm
Appearance Clear
Cure 40 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <4 ppm
Mix Ratio 1:1
Volatile Content 0.3 %
Comment Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

View more

GEL-3500 11,250 cP N/A 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

GEL-8100 535 cP N/A N/A 1:1 Download GEL-8100 data sheet N/A

Product Details

Property Average Result
Viscosity 535 cP (535 mPa*s)
Appearance Clear
Cure 1 hours / 100 °C
Mix Ratio 1:1
Specific Gravity 0.98

View more

GEL-8111 535 cP N/A N/A 1:1 Download GEL-8111 data sheet For applications requiring a low viscosity and low volatility soft gel

Product Details

Property Average Result
Appearance Clear
Cure 1 hour / 100°C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Refractive Index 1.40
Rheology Flowable / Self Leveling
Viscosity 535 cP (535 mPa*s)
Volatile Content 0.09 %

View more

GEL-8127 530 cP 8 mm N/A N/A Download GEL-8127 data sheet N/A

Product Details

Property Average Result
Viscosity 530 cP (530 mPa*s)
Penetration 8 mm
Appearance Translucent
Cure 35 minutes / 150 °C

View more

GEL-8136 450 cP 14 mm N/A N/A Download GEL-8136 data sheet N/A

Product Details

Property Average Result
Viscosity 450 cP (450 mPa*s)
Penetration 14 mm
Appearance Clear
Cure 60 minutes / 140 °C

View more

GEL-8150 500 cP 5 mm 4 hours 1:1 Download GEL-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 5 mm
Work Time 4 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 1 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

GEL-8170 600 cP 9 mm N/A 1:1 Download GEL-8170 data sheet Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

Product Details

Property Average Result
Viscosity 600 cP (600 mPa*s)
Penetration 9 mm
Appearance Translucent
Cure 90 minutes / 80 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

View more

GEL-8250 650 cP 5 mm 2 hours 1:1 Download GEL-8250 data sheet Soft Med Tack Gel;For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Work Time 2 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft Med Tack Gel;For applications requiring a broader operating temperature range.

View more

GEL1-8155 14,500 cP 0.4 mm N/A 1:1 Download GEL1-8155 data sheet Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Comment Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

View more

GEL8-8150 500 cP 4 mm 1.5 hours 1:1 Download GEL8-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 4 mm
Work Time 1.5 hours
Appearance Clear
Cure 30 minutes / 100 °C
Cure System Platinum
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 0.97
Comment Soft High Tack Gel

View more

LS-3238 1,500 cP N/A 11 hours 1:1 Download LS-3238 data sheet Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

Product Details

Property Average Result
Viscosity 1,500 cP (1,500 mPa*s)
Work Time 11 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Durometer 15 Type 00
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.38
Specific Gravity 1.28
Volatile Content 0.14 %
Comment Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

View more

LS-3441 14,500 cP 0.4 mm N/A 1:1 Download LS-3441 data sheet Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.41
Comment Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

View more

LS-3443 650 cP 5 mm N/A 1:1 Download LS-3443 data sheet Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volatile Content 0.35 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

View more

LS1-3252 360 cP N/A N/A N/A Download LS1-3252 data sheet 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

Product Details

Property Average Result
Viscosity 360 cP (360 mPa*s)
Appearance Clear
Cure 30 minutes / 150 °C
Durometer 25 Type 00
Refractive Index 1.52
Specific Gravity 1.07
Comment 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

View more

LS1-3443 2,500 cP 6 mm N/A N/A Download LS1-3443 data sheet N/A

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 6 mm
Appearance Clear
Specific Gravity 1

View more

LS3-3354 5,200 cP N/A 80 minutes 1:1 Download LS3-3354 data sheet Soft Gel;Excellent for phosphor coatings.

Product Details

Property Average Result
Viscosity 5,200 cP (5,200 mPa*s)
Work Time 80 minutes
Appearance Clear
Cure 1 minutes / 70 °C
Cure System Platinum
Durometer 60 Type 000
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.54
Comment Soft Gel;Excellent for phosphor coatings.

View more

MED-6311 500 cP 2.6 mm N/A 1:1 Download MED-6311 data sheet Low penetration, high strength gel

Product Details

Property Average Result
Penetration 2.6 mm
Viscosity 500 cP (500 mPa*s)
Mix Ratio 1:1
Appearance Clear
Cure 3.5 hours / 160 °C
Specific Gravity 0.97
Volatile Content 0.1 %
Comment Low penetration, high strength gel

View more

MED1-6300 1,000 cP 5 mm N/A 1:1 Download MED1-6300 data sheet Medium penetration, soft responsive gel

Product Details

Property Average Result
Penetration 5 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 1:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Non Volatile Content 99.9 %
Specific Gravity 0.98
Volatile Content 0.1 %
Comment Medium penetration, soft responsive gel

View more

MED2-6300 1,000 cP 10 mm N/A 1:1 Download MED2-6300 data sheet Low penetration, firm cohesive gel

Product Details

Property Average Result
Penetration 10 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 1:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Non Volatile Content 99.9 %
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 0.1 %
Comment Low penetration, firm cohesive gel

View more

MED3-6300 1,000 cP 15 mm N/A 3:1 Download MED3-6300 data sheet High penetration, soft responsive gel

Product Details

Property Average Result
Penetration 15 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 3:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Specific Gravity 0.97
Volatile Content 0.1 %
Comment High penetration, soft responsive gel

View more

MED3-6311 500 cP 2.6 mm N/A 3:1 Download MED3-6311 data sheet High Purity, Low Penetration, High Strength Gel

Product Details

Property Average Result
Penetration 2.6 mm
Viscosity 500 cP (500 mPa*s)
Mix Ratio 3:1
Appearance Translucent
Cure 3.5 hours / 160 °C
Cure System Platinum
Non Volatile Content 99.9 %
Specific Gravity 0.97
Volatile Content 0.1 %
Comment High Purity, Low Penetration, High Strength Gel

View more

Greases

Product Substrate Volatile Content Viscosity Data Sheet Comment
CV-9042 Glass / Metal / Plastic N/A N/A Download CV-9042 data sheet Thermally Conductive

Product Details

Property Average Result
Specific Gravity 1.61
Appearance White
Comment Thermally Conductive

View more

CV-9052 Glass / Metal / Plastic N/A N/A Download CV-9052 data sheet Volume Resistivity 1x1015 ohmcm, Thermally conductive

Product Details

Property Average Result
Specific Gravity 1.1
Appearance Gray
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Volume Resistivity 1x1015 ohmcm, Thermally conductive

View more

CV-9341 Glass / Metal / Plastic N/A N/A Download CV-9341 data sheet Thermally Conductive

Product Details

Property Average Result
Specific Gravity 2.3
Thermal Conductivity 0.7 W/(mK)
Appearance White
Comment Thermally Conductive

View more

G-9010 Glass / Metal / Plastic 0.34 % 1,100,000 cP Download G-9010 data sheet A stiff methyl silicone/Teflon grease for high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 1,100,000 cP (1,100,000 mPa*s)
Specific Gravity 1.14
Volatile Content 0.34 %
Appearance Gray
Flow Rate 2.7 in (68.58 mm)
Operating Temperature -40 °C / 230 °C
Comment A stiff methyl silicone/Teflon grease for high vacuum and pressure systems.

View more

G-9020 Glass / Metal / Plastic 0.3 % 310,000 cP Download G-9020 data sheet A medium consistency methyl silicone grease for high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 310,000 cP (310,000 mPa*s)
Specific Gravity 1.08
Volatile Content 0.3 %
Appearance Translucent
Operating Temperature -40 °C / 230 °C
Comment A medium consistency methyl silicone grease for high vacuum and pressure systems.

View more

G-9030 Glass / Metal / Plastic 0.3 % 980,100 cP Download G-9030 data sheet A stiff methyl grease used lubricating . 0.3% Weight loss. For high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 980,100 cP (980,100 mPa*s)
Specific Gravity 1.11
Volatile Content 0.3 %
Appearance Gray
Extrusion Rate 53 g/minute
Operating Temperature -40 °C / 230 °C
Comment A stiff methyl grease used lubricating . 0.3% Weight loss. For high vacuum and pressure systems.

View more

LS-1246 Glass / Metal / Plastic N/A N/A Download LS-1246 data sheet N/A

Product Details

Property Average Result
Specific Gravity 1.1
Appearance Clear
Refractive Index 1.46

View more

MED-6731 Silicone 0.6 % 2,000,000 cP Download MED-6731 data sheet High Consistency Methyl Fluoro Grease

Product Details

Property Average Result
Volatile Content 0.6 %
Viscosity 2,000,000 cP (2,000,000 mPa*s)
Substrate Silicone
Comment High Consistency Methyl Fluoro Grease

View more

MED-9011 Glass / Metal / Plastic 0.3 % 95,000 cP Download MED-9011 data sheet Low Consistency Grease

Product Details

Property Average Result
Volatile Content 0.3 %
Viscosity 95,000 cP (95,000 mPa*s)
Appearance Translucent
Non Volatile Content 99.4 %
Specific Gravity 1
Substrate Glass / Metal / Plastic
Comment Low Consistency Grease

View more

MED-9021 Glass / Metal / Plastic 0.5 % 300,000 cP Download MED-9021 data sheet Medium Consistency Grease

Product Details

Property Average Result
Volatile Content 0.5 %
Viscosity 300,000 cP (300,000 mPa*s)
Appearance White
Specific Gravity 1.08
Substrate Glass / Metal / Plastic
Comment Medium Consistency Grease

View more

MED-9031 Glass / Metal / Plastic 0.3 % 900,000 cP Download MED-9031 data sheet High Consistency Grease

Product Details

Property Average Result
Volatile Content 0.3 %
Viscosity 900,000 cP (900,000 mPa*s)
Appearance White
Specific Gravity 1.11
Substrate Glass / Metal / Plastic
Comment High Consistency Grease

View more

High Consistency Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
MED-2174 50 Type A 1,300 psi 750 % 225 ppi Download MED-2174 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 750 %
Tear 225 ppi (39.68 kN/m)
Appearance Clear
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 4 hours / 205 °C
Specific Gravity 1.15
Stress at Strain 325 psi / 200 % (2.24 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4014 15 Type A 700 psi 1,350 % 155 ppi Download MED-4014 data sheet Low modulus

Product Details

Property Average Result
Durometer 15 Type A
Tensile 700 psi (4.83 MPa)
Elongation 1,350 %
Tear 155 ppi (27.34 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 1.25 minutes
Cure Rate T90 2.5 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.08
Stress at Strain 40 psi / 200 % (0.28 MPa / 200 %)
Work Time 25 hours
Comment Low modulus

View more

MED-4019 55 Type A 1,290 psi 645 % 205 ppi Download MED-4019 data sheet Excellent adhesion and fatigue resistance

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,290 psi (8.9 MPa)
Elongation 645 %
Tear 205 ppi (36.2 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Specific Gravity 1.23
Stress at Strain 310 psi / 200 % (2.1 MPa / 200 %)
Work Time 5 hours
Comment Excellent adhesion and fatigue resistance

View more

MED-4020 25 Type A 1,400 psi 1,250 % 190 ppi Download MED-4020 data sheet Low modulus with high tear

Product Details

Property Average Result
Durometer 25 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 1,250 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.95 minutes
Cure Rate T90 2.3 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.1
Stress at Strain 75 psi / 200 % (0.52 MPa / 200 %)
Work Time 10 hours
Comment Low modulus with high tear

View more

MED-4025 30 Type A 1,300 psi 900 % 130 ppi Download MED-4025 data sheet Low tension set

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 900 %
Tear 130 ppi (22.93 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure Rate Scorch 0.75 minutes
Cure Rate T90 2.8 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 105 psi / 200 % (0.72 MPa / 200 %)
Work Time 1.5 hours
Comment Low tension set

View more

MED-4027 30 Type A 2,300 psi 1,050 % 235 ppi Download MED-4027 data sheet Ultra-high tensile strength

Product Details

Property Average Result
Durometer 30 Type A
Tensile 2,300 psi (15.86 MPa)
Elongation 1,050 %
Tear 235 ppi (41.45 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Work Time 2.5 hours
Comment Ultra-high tensile strength

View more

MED-4032 30 Type A 1,200 psi 1,100 % 160 ppi Download MED-4032 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 1,100 %
Tear 160 ppi (28.22 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 3.05 minutes
Mix Ratio 100:1:1
Specific Gravity 1.1
Stress at Strain 140 psi / 200 % (0.97 MPa / 200 %)
Work Time 8 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4035 35 Type A 1,565 psi 1,055 % 195 ppi Download MED-4035 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,565 psi (10.79 MPa)
Elongation 1,055 %
Tear 195 ppi (34.39 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 195 psi / 200 % (1.34 MPa / 200 %)
Work Time 2 hours
Comment High Tear Strength

View more

MED-4042 40 Type A 1,500 psi 1000 % 160 ppi Download MED-4042 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 1000 %
Tear 160 ppi (28.22 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.8 minutes
Cure Rate T90 2.45 minutes
Mix Ratio 100:1:1
Specific Gravity 1.11
Stress at Strain 230 psi / 200 % (1.59 MPa / 200 %)
Work Time 2 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4050 50 Type A 1,500 psi 985 % 250 ppi Download MED-4050 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 985 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent Gray
Cure 10 minutes / 115 °C
Cure Rate Scorch 1.1 minutes
Cure Rate T90 2.6 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 3.5 hours
Comment High Tear Strength

View more

MED-4052 50 Type A 1,445 psi 1100 % 230 ppi Download MED-4052 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,445 psi (9.97 MPa)
Elongation 1100 %
Tear 230 ppi (40.56 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.7 minutes
Cure Rate T90 2.25 minutes
Mix Ratio 100:1:1
Specific Gravity 1.16
Stress at Strain 280 psi / 200 % (1.93 MPa / 200 %)
Work Time 9 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4055 55 Type A 1,700 psi 900 % 300 ppi Download MED-4055 data sheet Ultra-high tear strength

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,700 psi (11.72 MPa)
Elongation 900 %
Tear 300 ppi (52.91 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 2.85 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.14
Stress at Strain 500 psi / 200 % (3.45 MPa / 200 %)
Work Time 2.5 hours
Comment Ultra-high tear strength

View more

MED-4062 60 Type A 1,400 psi 1000 % 250 ppi Download MED-4062 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 1000 %
Tear 250 ppi (44.09 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.7 minutes
Cure Rate T90 2.3 minutes
Mix Ratio 100:1:1
Specific Gravity 1.16
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 11 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4065 65 Type A 1,250 psi 1000 % 250 ppi Download MED-4065 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 65 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 1000 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent Tan
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.85 minutes
Cure Rate T90 2.65 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 350 psi / 200 % (2.41 MPa / 200 %)
Work Time 6 hours
Comment High Tear Strength

View more

MED-4070 70 Type A 1,430 psi 750 % 300 ppi Download MED-4070 data sheet Abrasion / Fatigue Resistant

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,430 psi (9.86 MPa)
Elongation 750 %
Tear 300 ppi (52.91 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure Rate Scorch 0.9 minutes
Cure Rate T90 2.7 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.19
Stress at Strain 600 psi / 200 % (4.14 MPa / 200 %)
Work Time 2 hours
Comment Abrasion / Fatigue Resistant

View more

MED-4072 70 Type A 1,100 psi 875 % 240 ppi Download MED-4072 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 875 %
Tear 240 ppi (42.33 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.9 minutes
Mix Ratio 100:1:1
Specific Gravity 1.22
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)
Work Time 4 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4080 80 Type A 1,150 psi 700 % 225 ppi Download MED-4080 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 700 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent Tan
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.8 minutes
Cure Rate T90 2.75 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)
Work Time 8 hours
Comment High Tear Strength

View more

MED-4082 80 Type A 1,150 psi 900 % 200 ppi Download MED-4082 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 900 %
Tear 200 ppi (35.27 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.6 minutes
Cure Rate T90 2.2 minutes
Mix Ratio 100:1:1
Specific Gravity 1.22
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Work Time 16 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4120 30 Type A 1,300 psi 950 % 140 ppi Download MED-4120 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 950 %
Tear 140 ppi (24.69 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 2.1 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4128 25 Type A 1,010 psi 800 % 70 ppi Download MED-4128 data sheet Low Tension Set, Uncatalyzed

Product Details

Property Average Result
Durometer 25 Type A
Tensile 1,010 psi (6.97 MPa)
Elongation 800 %
Tear 70 ppi (12.35 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.65 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 200 °C
Specific Gravity 1.11
Stress at Strain 90 psi / 200 % (0.62 MPa / 200 %)
Comment Low Tension Set, Uncatalyzed

View more

MED-4135 35 Type A 1,250 psi 800 % 110 ppi Download MED-4135 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 800 %
Tear 110 ppi (19.4 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 2.1 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 190 psi / 200 % (1.31 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4150 50 Type A 1,400 psi 750 % 190 ppi Download MED-4150 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 750 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.5 minutes
Cure Rate T90 1.9 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.16
Stress at Strain 250 psi / 200 % (1.72 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4174 50 Type A 1,200 psi 775 % 225 ppi Download MED-4174 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 775 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.7 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 4 hours / 205 °C
Specific Gravity 1.15
Stress at Strain 325 psi / 200 % (2.24 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4520 28 Type A 1,320 psi 950 % 135 ppi Download MED-4520 data sheet Uncatalyzed