Description
- Two-part, flowable, red RTV silicone
- 100: 0.5 Mix Ratio (Base: Curing Agent)
Applications
- For applications requiring low outgassing and minimal volatile condensables under extreme operating conditions to avoid condensation in sensitive devices
- As a sealing, caulking, adhesive or potting material in electronic and space applications where high vacuum environments are encountered
- For bonding solar cells to solar array panels
- For applications requiring a broader operating temperature range
Meets or exceeds the ASTM E 595 low outgas specifications outlined in NASA SP-R-0022A and European Space Agency PSS-014-702, with a TML of ≤1% and CVCM of ≤0.1%
Product Details
| Property | Average Result |
|---|---|
| Cure System | Alkoxy |
| Viscosity | 55,000 cP (55,000 mPa*s) |
| Lap Shear | 500 psi (3.45 MPa) |
| Durometer | 55 Type A |
| Appearance | Rust Red |
| Cte | |
| Cure | 7 days / RTV |
| Dielectric Strength | 825 volts/mil (32.18 kV/mm) |
| Elongation | 150 % |
| Mix Ratio | 100:0.5 |
| Specific Gravity | 1.49 |
| Tack Free Time | 8 hours |
| Tear | 40 ppi (7.05 kN/m) |
| Tensile | 950 psi (6.55 MPa) |
| Thermal Conductivity | 0.27 W/(mK) |
| Work Time | 3 hours |
| Comment | Pourable RTV Cure, * 1 )Primed Lap Shear 500 psi (3.4 MPa) |
Encapsulation Technology
Watch our CareSil team explain the breakthrough Encapsulation Technology and demonstrate how easy it is to create transformative formulations with CES.
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.