Description
- High tensile strength, low modulus high consistency silicone rubber
- Low tensile set and low hysteresis qualities
- Cures with heat via addition-cure chemistry
- 1:1 Mix Ratio (Part A: Part B)
Applications
- For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding
- Ideal for applications requiring low modulus and high strength properties such as balloons and bladders
- Can be considered as a replacement material for latex/natural rubber
1,050 %
Product Details
Property | Average Result |
---|---|
Durometer | 30 Type A |
Tensile | 2,300 psi (15.86 MPa) |
Elongation | 1,050 % |
Tear | 235 ppi (41.45 kN/m) |
Appearance | Translucent |
Cure | 10 minutes / 171 °C |
Mix Ratio | 1:1 |
Specific Gravity | 1.11 |
Stress at Strain | 100 psi / 200 % (0.69 MPa / 200 %) |
Work Time | 2.5 hours |
Comment | Ultra-high tensile strength |
The Strongest Silicone Elastomer Ever Developed
Dr. Jim Lambert, NuSil® Director of Research and Development, Biomaterials, introduces our breakthrough material that has a tensile strength of up to 50% greater than existing silicone elastomers on the market.
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.