Description
- Uncatalyzed, vinyl-functional, high consistency silicone elastomer
- Requires the addition of a peroxide catalyst to accomplish vulcanization
- Low tack surface
- Strained through a 400-mesh screen (minimum)
Applications
- For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding of parts
- Ideal for applications requiring a material with a low durometer, including: gaskets, seals, molded balloons, and catheter tips
NuSil Technology’s MED-4128 shall not be considered for use in human implantation for a period of greater than 29 days.
Product Details
Property | Average Result |
---|---|
Durometer | 25 Type A |
Tensile | 1,010 psi (6.97 MPa) |
Elongation | 800 % |
Tear | 70 ppi (12.35 kN/m) |
Appearance | Translucent |
Cure | 10 minutes / 116 °C |
Cure Rate Scorch | 0.55 minutes |
Cure Rate T90 | 1.65 minutes |
Cure System | Peroxide |
Mix Ratio | 1 PART |
Plasticity | |
Post Cure | 2 hours / 200 °C |
Specific Gravity | 1.11 |
Stress at Strain | 90 psi / 200 % (0.62 MPa / 200 %) |
Comment | Low Tension Set, Uncatalyzed |
The Strongest Silicone Elastomer Ever Developed
Dr. Jim Lambert, NuSil® Director of Research and Development, Biomaterials, introduces our breakthrough material that has a tensile strength of up to 50% greater than existing silicone elastomers on the market.
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.