Description
- Uncatalyzed, vinyl-functional, high consistency silicone elastomer
- Low durometer
- Requires the addition of a peroxide catalyst to accomplish vulcanization
- Strained through a 400-mesh screen (minimum)
Applications
- For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding
NuSil Technology’s MED-4135 shall not be considered for use in human implantation for a period of greater than 29 days.
Product Details
| Property | Average Result |
|---|---|
| Durometer | 35 Type A |
| Tensile | 1,250 psi (8.62 MPa) |
| Elongation | 800 % |
| Tear | 110 ppi (19.4 kN/m) |
| Appearance | Translucent |
| Cure | 5 minutes / 116 °C |
| Cure Rate Scorch | 0.55 minutes |
| Cure Rate T90 | 2.1 minutes |
| Cure System | Peroxide |
| Mix Ratio | 1 PART |
| Plasticity | |
| Post Cure | 2 hours / 177 °C |
| Specific Gravity | 1.1 |
| Stress at Strain | 190 psi / 200 % (1.31 MPa / 200 %) |
| Comment | Uncatalyzed |