Description
- Two-part, optically clear silicone system
- Based on a methyl silicone polymer
- Low viscosity
- 1:1 Mix Ratio (Part A:B)
Applications
- For bonding, casting or injection molding of high performance optical components
- For applications requiring index matching at 1.40
- For photonics applications requiring low outgassing and minimal volatile condensables to avoid condensation in sensitive devices
Product Details
| Property | Average Result |
|---|---|
| Cure System | Platinum |
| Viscosity | 3,125 cP (3,125 mPa*s) |
| Durometer | 50 Type A |
| Tensile | 850 psi (5.86 MPa) |
| Elongation | 90 % |
| Appearance | Clear |
| Cte | |
| Cure | 15 minutes / 150 °C |
| Dielectric Strength | 520 volts/mil (20.28 kV/mm) |
| Ionic Content Cl | <5 ppm |
| Ionic Content K | <2 ppm |
| Ionic Content Na | <4 ppm |
| Lap Shear | 200 psi (1.38 MPa) |
| Mix Ratio | 1:1 |
| Refractive Index | 1.40 |
| Specific Gravity | 1.02 |
| Tack Free Time | 6 hours |
| Volume Resistivity | 1,100,000,000,000,000 ohmcm |
| Work Time | 3 hours |
| Comment | RTV; Low volatility |
Contact NuSil™ to Order Now
For over 40 years, the NuSil brand has offered a wide range of high-purity silicones. Our team is ready to collaborate with you to provide silicone solutions to satisfy your unique requirements. For additional guidance during your selection process, or to order a sample, contact NuSil today.
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.