Adhesives/Sealants

Product Cure System Rheology Work Time Durometer Data Sheet Comment
CV-1142 Oxime Thixotropic / non-slump N/A 45 Type A Download CV-1142 data sheet For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 35 g/minute
Lap Shear 375 psi (2.59 MPa)
Durometer 45 Type A
Appearance Translucent
Cure 7 days / RTV
Dielectric Strength 1,100 volts/mil (42.9 kV/mm)
Elongation 300 %
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.11
Tack Free Time 20 minutes
Tensile 700 psi (4.83 MPa)
Comment For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

View more

CV-2187 Platinum Flowable / Self Leveling 3 hours 35 Type A Download CV-2187 data sheet Tough, self leveling and good adhesion to various metals.

Product Details

Property Average Result
Cure System Platinum
Viscosity 90,000 cP (90,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 400 %
Mix Ratio 10:1
Specific Gravity 1.1
Tack Free Time 15 hours
Tear 75 ppi (13.23 kN/m)
Tensile 925 psi (6.38 MPa)
Work Time 3 hours
Comment Tough, self leveling and good adhesion to various metals.

View more

CV-2289 Platinum Flowable / Self Leveling 30 minutes 30 Type A Download CV-2289 data sheet Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 50,000 cP (50,000 mPa*s)
Lap Shear 400 psi (2.76 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Tensile 750 psi (5.17 MPa)
Work Time 30 minutes
Comment Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

View more

CV-2680-12 Platinum N/A N/A N/A Download CV-2680-12 data sheet Low Outgassing version of R-2682-12.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 250 psi (1.72 MPa)
Appearance Translucent
Application Life 4 hours
Cure 4 hours / 65 °C
Elongation 400 %
Tear 115 ppi (20.28 kN/m)
Tensile 1,450 psi (10 MPa)
Comment Low Outgassing version of R-2682-12.

View more

CV-2686-12 Platinum N/A N/A N/A Download CV-2686-12 data sheet Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

Product Details

Property Average Result
Cure System Platinum
Appearance Black
Cure 4 hours / 65 °C
Volume Resistivity 150 ohmcm
Comment Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

View more

CV-2688-12 Platinum Thixotropic / Non-slump N/A N/A Download CV-2688-12 data sheet For applications requiring shorter work times, easy clean-up, and consistent bond thickness

Product Details

Property Average Result
Appearance Translucent
Cure 4 hours / 65 °C
Cure System Platinum
Cure Type RTV
Elongation 850 %
Lap Shear 250 psi (1.7 MPa)
Rheology Thixotropic / Non-slump
Substrate Primerless: ABS / Aluminum / Glass / Metal / PEEK / Plastic / PMMA / Polycarbonate / Polyetherimide / Polymide / Polyurethane / Silicone / Stainless steel / Titanium
Tear 115 ppi (20.3 kN/m)
Tensile 1,450 psi (10.0 MPa)

View more

CV1-1142 Oxime Flowable / Self Leveling N/A 30 Type A Download CV1-1142 data sheet Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

Product Details

Property Average Result
Cure System Oxime
Viscosity 13,000 cP (13,000 mPa*s)
Extrusion Rate 70 g/minute
Lap Shear 65 psi (0.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 200 %
Specific Gravity 1.05
Tensile 400 psi (2.76 MPa)
Comment Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

View more

CV1-2289-1 Platinum Flowable / Self Leveling 4 hours 30 Type A Download CV1-2289-1 data sheet White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 52,500 cP (52,500 mPa*s)
Lap Shear 450 psi (3.1 MPa)
Durometer 30 Type A
Appearance White
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 17 hours
Tensile 750 psi (5.17 MPa)
Work Time 4 hours
Comment White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

View more

CV2-1142 Oxime Thixotropic / non-slump N/A 50 Type A Download CV2-1142 data sheet Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

Product Details

Property Average Result
Cure System Oxime
Durometer 50 Type A
Appearance Translucent
Cure 7 days / RTV
Comment Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

View more

CV2-2289-1 Platinum Flowable / Self Leveling N/A 30 Type A Download CV2-2289-1 data sheet White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 12,300 cP (12,300 mPa*s)
Lap Shear 300 psi (2.07 MPa)
Durometer 30 Type A
Appearance White
Cure 4 hours / 65 °C
Elongation 250 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 20 hours
Tensile 450 psi (3.1 MPa)
Comment White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

View more

CV2-2646 Alkoxy Flowable / Self Leveling 2 hours 75 Type A Download CV2-2646 data sheet 0.003 ohmcm at 200 C

Product Details

Property Average Result
Cure System Alkoxy
Lap Shear 185 psi (1.28 MPa)
Durometer 75 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 70 %
Flow Rate 4 in (101.6 mm)
Mix Ratio 100:0.5
Specific Gravity 3.23
Tear 55 ppi (9.7 kN/m)
Tensile 300 psi (2.07 MPa)
Thermal Conductivity 1.5 W/(mK)
Volume Resistivity 0 ohmcm
Work Time 2 hours
Comment 0.003 ohmcm at 200 C

View more

CV7-1142-1 Oxime Flowable / Self Leveling N/A 40 Type A Download CV7-1142-1 data sheet Recommended for extended operation at elevated temperatures.

Product Details

Property Average Result
Cure System Oxime
Rheology Flowable / Self Leveling
Durometer 40 Type A
Appearance White
Cure 7 days / RTV
Cure Type RTV
Dielectric Strength 1,180 volts/mil (46.02 kV/mm)
Elongation 300 %
Extrusion Rate 20 g/minute
Flow Rate 0.7 in (17.78 mm)
Mix Ratio 1 PART
Specific Gravity 1.13
Tack Free Time 20 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 700 psi (4.83 MPa)

View more

EPM-2411-2 Platinum Thixotropic / non-slump N/A 20 Type A Download EPM-2411-2 data sheet Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 300,000 cP (300,000 mPa*s)
Extrusion Rate 0.9 g/minute
Durometer 20 Type A
Appearance Black
Cure 15 minutes / 200 °C
Elongation 700 %
Mix Ratio 1 PART
Specific Gravity 1.15
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 50 ppi (8.82 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

View more

EPM-2412 Platinum Flowable / Self Leveling 20 minutes 30 Type A Download EPM-2412 data sheet Mobile Devices, Displace

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 0.08 g/minute
Durometer 30 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Elongation 450 %
Tensile 850 psi (5.86 MPa)
Thermal Conductivity 0.18 W/(mK)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 20 minutes
Comment Mobile Devices, Displace

View more

EPM-2461 Platinum Thixotropic / non-slump 1 minutes 30 Type A Download EPM-2461 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Viscosity 675,000 cP (675,000 mPa*s)
Lap Shear 325 psi (2.24 MPa)
Durometer 30 Type A
Appearance Black
Cure 24 hours / RTV
Elongation 350 %
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <6 ppm
Mix Ratio 1:1
Operating Temperature -100 °C / 300 °C
Specific Gravity 1.05
Tear 30 ppi (5.29 kN/m)
Tensile 500 psi (3.45 MPa)
Thermal Conductivity 0.22 W/(mK)
Volume Resistivity 535 ohmcm
Work Time 1 minutes
Comment Carbon filled.

View more

EPM-2462 Platinum Thixotropic / non-slump 2.75 hours 85 Type A Download EPM-2462 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 186,200 cP (186,200 mPa*s)
Durometer 85 Type A
Appearance Tan
Cure 30 minutes / 150 C
Elongation 70 %
Ionic Content Cl <5 ppm
Ionic Content K <7 ppm
Ionic Content Na <5 ppm
Mix Ratio 20:1
Specific Gravity 3.39
Tensile 525 psi (3.62 MPa)
Thermal Conductivity 1.2 W/(mK)
Volume Resistivity 0.01 ohmcm
Work Time 2.75 hours

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

R-1130 Oxime Thixotropic / non-slump N/A 35 Type A Download R-1130 data sheet Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 70 g/minute
Lap Shear 485 psi (3.34 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 325 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.1
Tack Free Time 25 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

View more

R-1140 Acetoxy Thixotropic / non-slump N/A 30 Type A Download R-1140 data sheet Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 350 %
Flow Rate 1.5 in (38.1 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.09
Tack Free Time 7 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

View more

R-1400 Platinum Thixotropic / non-slump N/A 19 Type A Download R-1400 data sheet Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400,000 cP (400,000 mPa*s)
Extrusion Rate 120 g/minute
Durometer 19 Type A
Appearance Black
Cure 15 minutes / 200 °C
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Elongation 750 %
Mix Ratio 1 PART
Specific Gravity 1.18
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 110 ppi (19.4 kN/m)
Tensile 825 psi (5.69 MPa)
Comment Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

View more

R-2141 N/A Flowable / Self Leveling 1.5 hours 40 Type A Download R-2141 data sheet N/A

Product Details

Property Average Result
Viscosity 180,000 cP (180,000 mPa*s)
Durometer 40 Type A
Appearance Translucent
Dielectric Strength 630 volts/mil (24.57 kV/mm)
Elongation 250 %
Flow Rate 0.3 in (7.62 mm)
Specific Gravity 1.1
Tack Free Time 4 hours
Tensile 650 psi (4.48 MPa)
Volatile Content 0.3 %
Work Time 1.5 hours

View more

R-2145 Platinum Flowable / Self Leveling 15 minutes 45 Type A Download R-2145 data sheet Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 180 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 15 minutes
Comment Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

View more

R-2160 Platinum Flowable / Self Leveling 1.5 hours 20 Type A Download R-2160 data sheet Iron Red, flowable legacy high performance elastomer at elevated temperatures.

Product Details

Property Average Result
Cure System Platinum
Viscosity 280,000 cP (280,000 mPa*s)
Durometer 20 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Elongation 625 %
Mix Ratio 10:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 315 °C
Specific Gravity 1.2
Tear 140 ppi (24.69 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 1.5 hours
Comment Iron Red, flowable legacy high performance elastomer at elevated temperatures.

View more

R-2186 Platinum Flowable / Self Leveling 2.5 hours 30 Type A Download R-2186 data sheet Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 83,000 cP (83,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 640 volts/mil (24.96 kV/mm)
Elongation 450 %
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 100 ppi (17.64 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 2.5 hours
Comment Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more

R-2550 Alkoxy Flowable / Self Leveling 6 hours 35 Type A Download R-2550 data sheet Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 9,000 cP (9,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 175 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.08
Tear 20 ppi (3.53 kN/m)
Tensile 500 psi (3.45 MPa)
Work Time 6 hours
Comment Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2560 Alkoxy Flowable / Self Leveling 1 minutes 55 Type A Download R-2560 data sheet Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 31,000 cP (31,000 mPa*s)
Lap Shear 385 psi (2.66 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 125 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Specific Gravity 1.41
Tack Free Time 2 hours
Tensile 700 psi (4.83 MPa)
Work Time 1 minutes
Comment Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2630 Platinum Flowable / Self Leveling 15 hours 60 Type A Download R-2630 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Durometer 60 Type A
Appearance Black
Cure 30 minutes / 150 °C
Elongation 95 %
Mix Ratio 10:1
Operating Temperature -65 °C / 200 °C
Specific Gravity 1.1
Tear 40 ppi (7.05 kN/m)
Tensile 690 psi (4.76 MPa)
Volume Resistivity 6 ohmcm
Work Time 15 hours
Comment Carbon filled.

View more

R-2634 Alkoxy Thixotropic / non-slump 3 hours 80 Type A Download R-2634 data sheet 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

Product Details

Property Average Result
Cure System Alkoxy
Extrusion Rate 160 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 80 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 90 %
Flow Rate 1.2 in (30.48 mm)
Mix Ratio 100:0.5
Specific Gravity 3.41
Tear 50 ppi (8.82 kN/m)
Tensile 250 psi (1.72 MPa)
Volume Resistivity 0 ohmcm
Work Time 3 hours
Comment 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

View more

R-2682-12 Platinum N/A N/A N/A Download R-2682-12 data sheet For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 100 psi (0.69 MPa)
Appearance Translucent
Application Life 4 hours
Cure 4 hours / 65 °C
Comment For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

View more

R1-2145 Platinum Flowable / Self Leveling 1 minutes 45 Type A Download R1-2145 data sheet Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 140 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 190 ppi (33.51 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 1 minutes
Comment Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

View more

R31-2186 Platinum Flowable / Self Leveling 15 minutes 20 Type A Download R31-2186 data sheet RTV Primerless Adhesive;Very fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 142,500 cP (142,500 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 110 psi (0.76 MPa)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 775 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Tear 125 ppi (22.05 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 15 minutes
Comment RTV Primerless Adhesive;Very fast cure.

View more

R32-2186 Platinum Flowable / Self Leveling 15 hours 15 Type A Download R32-2186 data sheet Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 170,000 cP (170,000 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 150 psi (1.03 MPa)
Durometer 15 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 850 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Stress at Strain 35 psi / 100 % (0.24 MPa / 100 %)
Tear 125 ppi (22.05 kN/m)
Tensile 975 psi (6.72 MPa)
Work Time 15 hours
Comment Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

View more

R33-2186 Platinum Flowable / Self Leveling 2 hours 20 Type A Download R33-2186 data sheet RTV Primerless Adhesive;Fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 124,350 cP (124,350 mPa*s)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 725 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 150 ppi (26.46 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment RTV Primerless Adhesive;Fast cure.

View more

R33-2186-1 N/A Flowable / Self Leveling 2 hours 20 Type A Download R33-2186-1 data sheet N/A

Product Details

Property Average Result
Viscosity 80,000 cP (80,000 mPa*s)
Durometer 20 Type A
Appearance White
Elongation 740 %
Specific Gravity 1.12
Tear 135 ppi (23.81 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours

View more

R4-1140 Acetoxy Flowable / Self Leveling N/A 25 Type A Download R4-1140 data sheet Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 100 g/minute
Durometer 25 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 750 %
Flow Rate 2 in (50.8 mm)
Mix Ratio 1 PART
Specific Gravity 1.12
Stress at Strain 110 psi / N/A (0.76 MPa / N/A)
Tack Free Time 10 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Volatile Content 2.4 %
Comment Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

View more

SCV-2585 Platinum Flowable / Self Leveling 1 hours 35 Type A Download SCV-2585 data sheet Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 77,000 cP (77,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.11
Tack Free Time 7 hours
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Work Time 1 hours
Comment Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more