Adhesives/Sealants

Apply

  • Show more

Add filters

Adhesives/Sealants

Refine results
Product Cure System Rheology Work Time Durometer Data Sheet Comment
CF2-3521-2 Platinum Thixotropic / non-slump 1 hours 35 Type A Download CF2-3521-2 data sheet Fuel Resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 117 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 35 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 265 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.28
Tensile 600 psi (4.14 MPa)
Work Time 1 hours
Comment Fuel Resistance

View more

CF5-3521-2 Platinum Thixotropic / non-slump 3.5 hours 30 Type A Download CF5-3521-2 data sheet 50% M fluoro. Black and will RTV in 48 hrs

Product Details

Property Average Result
Cure System Platinum
Viscosity 240,000 cP (240,000 mPa*s)
Durometer 30 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 275 %
Mix Ratio 1:1
Specific Gravity 1.3
Tear 35 ppi (6.17 kN/m)
Tensile 550 psi (3.79 MPa)
Work Time 3.5 hours
Comment 50% M fluoro. Black and will RTV in 48 hrs

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS-3730-11 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-11 data sheet Lap Shear after 7 days *1) 275 psi (1.9 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 275 psi (1.9 MPa)
Durometer 40 Type A
Appearance Dark Gray
Cure 72 hours / RTV
Elongation 275 %
Mix Ratio 1 PART
Specific Gravity 1.48
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Lap Shear after 7 days *1) 275 psi (1.9 MPa)

View more

FS-3730-2 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-2 data sheet Lap Shear after 7 days *3) 300 psi (2.1 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 200 g/minute
Lap Shear 285 psi (1.97 MPa)
Durometer 40 Type A
Appearance Black
Cure 72 hours / RTV
Elongation 315 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.41
Tack Free Time 10 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 650 psi (4.48 MPa)
Comment Lap Shear after 7 days *3) 300 psi (2.1 MPa)

View more

FS-3775 Acetoxy Flowable / Self Leveling N/A 30 Type A Download FS-3775 data sheet High Temperature, Fuel Resistant

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 250 g/minute
Lap Shear 210 psi (1.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.29
Tack Free Time 8 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 450 psi (3.1 MPa)
Comment High Temperature, Fuel Resistant

View more

FS1-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS1-3730 data sheet Bonds Aggressively

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 150 g/minute
Lap Shear 275 psi (1.9 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / 25 °C
Elongation 425 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.4
Tack Free Time 30 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Bonds Aggressively

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

FS9-3521 Platinum Flowable / Self Leveling 3 hours 29 Type A Download FS9-3521 data sheet 100% F, For applications requiring fuel and solvent resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 50 g/minute
Lap Shear 280 psi (1.93 MPa)
Durometer 29 Type A
Appearance Brown
Cure 24 hours / RTV
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.4
Tensile 750 psi (5.17 MPa)
Work Time 3 hours
Comment 100% F, For applications requiring fuel and solvent resistance

View more

R-1130 Oxime Thixotropic / non-slump N/A 35 Type A Download R-1130 data sheet Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 70 g/minute
Lap Shear 485 psi (3.34 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 325 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.1
Tack Free Time 25 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

View more

R-1140 Acetoxy Thixotropic / non-slump N/A 30 Type A Download R-1140 data sheet Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 350 %
Flow Rate 1.5 in (38.1 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.09
Tack Free Time 7 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

View more

R-2145 Platinum Flowable / Self Leveling 15 minutes 45 Type A Download R-2145 data sheet Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 180 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 15 minutes
Comment Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

View more

R-2160 Platinum Flowable / Self Leveling 1.5 hours 20 Type A Download R-2160 data sheet Iron Red, flowable legacy high performance elastomer at elevated temperatures.

Product Details

Property Average Result
Cure System Platinum
Viscosity 280,000 cP (280,000 mPa*s)
Durometer 20 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Elongation 625 %
Mix Ratio 10:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 315 °C
Specific Gravity 1.2
Tear 140 ppi (24.69 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 1.5 hours
Comment Iron Red, flowable legacy high performance elastomer at elevated temperatures.

View more

R-2550 Alkoxy Flowable / Self Leveling 6 hours 35 Type A Download R-2550 data sheet Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 9,000 cP (9,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 175 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.08
Tear 20 ppi (3.53 kN/m)
Tensile 500 psi (3.45 MPa)
Work Time 6 hours
Comment Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2560 Alkoxy Flowable / Self Leveling 1 minutes 55 Type A Download R-2560 data sheet Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 31,000 cP (31,000 mPa*s)
Lap Shear 385 psi (2.66 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 125 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Specific Gravity 1.41
Tack Free Time 2 hours
Tensile 700 psi (4.83 MPa)
Work Time 1 minutes
Comment Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2630 Platinum Flowable / Self Leveling 15 hours 60 Type A Download R-2630 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Durometer 60 Type A
Appearance Black
Cure 30 minutes / 150 °C
Elongation 95 %
Mix Ratio 10:1
Operating Temperature -65 °C / 200 °C
Specific Gravity 1.1
Tear 40 ppi (7.05 kN/m)
Tensile 690 psi (4.76 MPa)
Volume Resistivity 6 ohmcm
Work Time 15 hours
Comment Carbon filled.

View more

R-2682-12 Platinum N/A N/A N/A Download R-2682-12 data sheet For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 100 psi (0.69 MPa)
Appearance Translucent
Application Life 4 hours
Cure 4 hours / 65 °C
Comment For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

View more

R1-2145 Platinum Flowable / Self Leveling 1 minutes 45 Type A Download R1-2145 data sheet Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 140 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 190 ppi (33.51 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 1 minutes
Comment Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

View more

R1-2680-4 Platinum N/A N/A N/A Download R1-2680-4 data sheet For applications requiring shorter work times, easy clean-up, and consistent bond thickness

Product Details

Property Average Result
Cure System Platinum
Appearance Translucent
Cure 4 hours / RTV
Comment For applications requiring shorter work times, easy clean-up, and consistent bond thickness

View more

R33-2186 Platinum Flowable / Self Leveling 2 hours 20 Type A Download R33-2186 data sheet RTV Primerless Adhesive;Fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 124,350 cP (124,350 mPa*s)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 725 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 150 ppi (26.46 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment RTV Primerless Adhesive;Fast cure.

View more

R33-2186-1 N/A Flowable / Self Leveling 2 hours 20 Type A Download R33-2186-1 data sheet N/A

Product Details

Property Average Result
Viscosity 80,000 cP (80,000 mPa*s)
Durometer 20 Type A
Appearance White
Elongation 740 %
Specific Gravity 1.12
Tear 135 ppi (23.81 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours

View more

R4-1140 Acetoxy Flowable / Self Leveling N/A 25 Type A Download R4-1140 data sheet Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 100 g/minute
Durometer 25 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 750 %
Flow Rate 2 in (50.8 mm)
Mix Ratio 1 PART
Specific Gravity 1.12
Stress at Strain 110 psi / N/A (0.76 MPa / N/A)
Tack Free Time 10 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Volatile Content 2.4 %
Comment Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

View more