Product Cure System Rheology Work Time Durometer Data Sheet Comment
CF2-3521-2 Platinum Thixotropic / non-slump 1 hours 35 Type A Download CF2-3521-2 data sheet Fuel Resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 117 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 35 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 265 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.28
Tensile 600 psi (4.14 MPa)
Work Time 1 hours
Comment Fuel Resistance

View more

CF5-3521-2 Platinum Thixotropic / non-slump 3.5 hours 30 Type A Download CF5-3521-2 data sheet 50% M fluoro. Black and will RTV in 48 hrs

Product Details

Property Average Result
Cure System Platinum
Viscosity 240,000 cP (240,000 mPa*s)
Durometer 30 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 275 %
Mix Ratio 1:1
Specific Gravity 1.3
Tear 35 ppi (6.17 kN/m)
Tensile 550 psi (3.79 MPa)
Work Time 3.5 hours
Comment 50% M fluoro. Black and will RTV in 48 hrs

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS-3730-11 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-11 data sheet Lap Shear after 7 days *1) 275 psi (1.9 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 275 psi (1.9 MPa)
Durometer 40 Type A
Appearance Dark Gray
Cure 72 hours / RTV
Elongation 275 %
Mix Ratio 1 PART
Specific Gravity 1.48
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Lap Shear after 7 days *1) 275 psi (1.9 MPa)

View more

FS-3730-2 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-2 data sheet Lap Shear after 7 days *3) 300 psi (2.1 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 200 g/minute
Lap Shear 285 psi (1.97 MPa)
Durometer 40 Type A
Appearance Black
Cure 72 hours / RTV
Elongation 315 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.41
Tack Free Time 10 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 650 psi (4.48 MPa)
Comment Lap Shear after 7 days *3) 300 psi (2.1 MPa)

View more

FS-3775 Acetoxy Flowable / Self Leveling N/A 30 Type A Download FS-3775 data sheet High Temperature, Fuel Resistant

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 250 g/minute
Lap Shear 210 psi (1.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.29
Tack Free Time 8 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 450 psi (3.1 MPa)
Comment High Temperature, Fuel Resistant

View more

FS1-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS1-3730 data sheet Bonds Aggressively

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 150 g/minute
Lap Shear 275 psi (1.9 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / 25 °C
Elongation 425 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.4
Tack Free Time 30 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Bonds Aggressively

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

FS9-3521 Platinum Flowable / Self Leveling 3 hours 29 Type A Download FS9-3521 data sheet 100% F, For applications requiring fuel and solvent resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 50 g/minute
Lap Shear 280 psi (1.93 MPa)
Durometer 29 Type A
Appearance Brown
Cure 24 hours / RTV
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.4
Tensile 750 psi (5.17 MPa)
Work Time 3 hours
Comment 100% F, For applications requiring fuel and solvent resistance

View more

Coatings/Dispersions

Product Cure System Durometer Data Sheet Comment
Acetoxy 40 Type A Download data sheet 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

Product Details

Property Average Result
Appearance Gray
Tack Free Time 20 minutes
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 40 Type A
Elongation 325 %
Lap Shear 290 psi (2 MPa)
Specific Gravity 1.48
Tear 45 ppi (7.94 kN/m)
Tensile 725 psi (5 MPa)
Comment 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

R-3930 Acetoxy 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

R-3975 Acetoxy 25 Type A Download R-3975 data sheet Dispersion Coating, 60% Solids

Product Details

Property Average Result
Viscosity 1,625 cP (1,625 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.29
Tear 35 ppi (6.17 kN/m)
Tensile 425 psi (2.93 MPa)
Comment Dispersion Coating, 60% Solids

View more

R1-3930-1 Acetoxy 37 Type A Download R1-3930-1 data sheet Slight addition of heat will accelerate cure

Product Details

Property Average Result
Appearance White
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 37 Type A
Elongation 334 %
Mix Ratio 1 PART
Tack Free Time 273 minutes
Tear 52 ppi (9 kN/m)
Tensile 739 psi (5.09 MPa)
Comment Slight addition of heat will accelerate cure

View more

R4-3930-11 Acetoxy 45 Type A Download R4-3930-11 data sheet For protecting or bonding hardware components exposed to gasoline or aviation fuels

Product Details

Property Average Result
Appearance Gray
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 45 Type A
Elongation 480 %
Mix Ratio 1:1
Tear 71 ppi (13 kN/m)
Tensile 750 psi (5 MPa)
Comment For protecting or bonding hardware components exposed to gasoline or aviation fuels

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

Gels

Product Viscosity Work Time Mix Ratio Data Sheet Comment
GEL-3500 11,250 cP 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

Liquid Silicone Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
FS-3511 30 Type A 1,150 psi 335 % 60 ppi Download FS-3511 data sheet LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

Product Details

Property Average Result
Cure System Platinum
Durometer 30 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 335 %
Tear 60 ppi (10.58 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Extrusion Rate 35 g/minute
Mix Ratio 1:1
Specific Gravity 1.39
Work Time 24 hours
Comment LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CF1-3800 1.25 W/(mK) 15:1 N/A N/A Platinum Download CF1-3800 data sheet 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.25 W/(mK)
Cure System Platinum
Tensile 125 psi (0.86 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 50 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.53
Work Time 90 minutes
Comment 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)