Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
R-1505 8 ohmcm N/A Oxime 75 Type A 525 psi Download R-1505 data sheet 8 ohmcm. Static Dissipation

Product Details

Property Average Result
Volume Resistivity 8 ohmcm
Cure System Oxime
Durometer 75 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 7 days / 25 °C
Dielectric Strength 10 volts/mil (0.39 kV/mm)
Elongation 25 %
Flow Rate 0.1 in (2.54 mm)
Lap Shear 290 psi (2 MPa)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.23
Tack Free Time 10 minutes
Thermal Conductivity 0.3 W/(mK)
Comment 8 ohmcm. Static Dissipation

View more

R-2631 70 ohmcm N/A Platinum 45 Type A 615 psi Download R-2631 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 70 ohmcm
Cure System Platinum
Durometer 45 Type A
Tensile 615 psi (4.24 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 275 %
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Tear 55 ppi (9.7 kN/m)
Comment Carbon filled.

View more

R-2637 0.01 ohmcm N/A Platinum 60 Type A 210 psi Download R-2637 data sheet Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 60 Type A
Tensile 210 psi (1.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Dielectric Strength 5 volts/mil (0.2 kV/mm)
Elongation 275 %
Mix Ratio 20:1
Specific Gravity 3.6
Tack Free Time 5 hours
Thermal Conductivity 1.5 W/(mK)
Work Time 4 hours
Comment Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CF1-3800 1.25 W/(mK) 15:1 N/A N/A Platinum Download CF1-3800 data sheet 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.25 W/(mK)
Cure System Platinum
Tensile 125 psi (0.86 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 50 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.53
Work Time 90 minutes
Comment 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

View more

R-2930 1.46 W/(mK) 15:1 N/A N/A Platinum Download R-2930 data sheet Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.46 W/(mK)
Cure System Platinum
Tensile 260 psi (1.79 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 880 volts/mil (34.32 kV/mm)
Durometer 80 Type A
Elongation 20 %
Flow Rate 0.3 inches (7.62 mm)
Mix Ratio 15:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.55
Work Time 3 hours
Comment Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

View more

R-2939 0.75 W/(mK) 15:1 70,000 cP N/A Platinum Download R-2939 data sheet 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 70,000 cP (70,000 mPa*s)
Cure System Platinum
Tensile 300 psi (2.07 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 810 volts/mil (31.59 kV/mm)
Durometer 70 Type A
Elongation 70 %
Mix Ratio 15:1
Specific Gravity 1.34
Tear 45 ppi (7.94 kN/m)
Work Time 4 hours
Comment 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

View more

R-2940 0.84 W/(mK) 20:1 N/A N/A Platinum Download R-2940 data sheet Smooth Paste;0.8 W/mK, 5 hr. pot life.

Product Details

Property Average Result
Thermal Conductivity 0.84 W/(mK)
Cure System Platinum
Tensile 700 psi (4.83 MPa)
Appearance Gray
Cure 30 minutes / 150 °C
Dielectric Strength 450 volts/mil (17.55 kV/mm)
Durometer 90 Type A
Elongation 35 %
Mix Ratio 20:1
Specific Gravity 2.41
Tack Free Time 24 hours
Tear 65 ppi (11.46 kN/m)
Work Time 5 hours
Comment Smooth Paste;0.8 W/mK, 5 hr. pot life.

View more

R-2949 0.75 W/(mK) 15:1 75,000 cP N/A Platinum Download R-2949 data sheet For applications requiring a broader operating temperature range. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 75,000 cP (75,000 mPa*s)
Cure System Platinum
Tensile 275 psi (1.9 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 920 volts/mil (35.88 kV/mm)
Durometer 75 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.37
Tear 45 ppi (7.94 kN/m)
Work Time 3.5 hours
Comment For applications requiring a broader operating temperature range. (Contains Boron Nitride)