Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV1-1146-2 Oxime 1,125 cP N/A N/A Download CV1-1146-2 data sheet N/A

Product Details

Property Average Result
Viscosity 1,125 cP (1,125 mPa*s)
Appearance Black
Tack Free Time 2 hours
Cure System Oxime

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2180-2 Platinum 3,275 cP 20 % 45 Type A Download R-2180-2 data sheet Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

Product Details

Property Average Result
Viscosity 3,275 cP (3,275 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 30 minutes / RTV 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 45 Type A
Elongation 1,000 %
Mix Ratio 1:1
Stress at Strain 140 psi / 100 % (0.97 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,650 psi (11.38 MPa)
Comment Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

R-3975 Acetoxy 1,625 cP 60 % 25 Type A Download R-3975 data sheet Dispersion Coating, 60% Solids

Product Details

Property Average Result
Viscosity 1,625 cP (1,625 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.29
Tear 35 ppi (6.17 kN/m)
Tensile 425 psi (2.93 MPa)
Comment Dispersion Coating, 60% Solids

View more

R1-3930-1 Acetoxy N/A N/A 37 Type A Download R1-3930-1 data sheet Slight addition of heat will accelerate cure

Product Details

Property Average Result
Appearance White
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 37 Type A
Elongation 334 %
Mix Ratio 1 PART
Tack Free Time 273 minutes
Tear 52 ppi (9 kN/m)
Tensile 739 psi (5.09 MPa)
Comment Slight addition of heat will accelerate cure

View more

R3-1075 Oxime 3,300 cP 60 % 40 Type A Download R3-1075 data sheet Dispersion Coating / Conformal, 60% Solids

Product Details

Property Average Result
Viscosity 3,300 cP (3,300 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 80 minutes
Cure 7 days / 25 °C
Cure System Oxime
Dielectric Strength 1,250 volts/mil (48.75 kV/mm)
Durometer 40 Type A
Elongation 350 %
Mix Ratio 1 PART
Operating Temperature -65 °C / 240 °C
Solvent Xylene
Specific Gravity 1.06
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Dispersion Coating / Conformal, 60% Solids

View more

R4-3930-11 Acetoxy N/A N/A 45 Type A Download R4-3930-11 data sheet For protecting or bonding hardware components exposed to gasoline or aviation fuels

Product Details

Property Average Result
Appearance Gray
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 45 Type A
Elongation 480 %
Mix Ratio 1:1
Tear 71 ppi (13 kN/m)
Tensile 750 psi (5 MPa)
Comment For protecting or bonding hardware components exposed to gasoline or aviation fuels

View more